PA66 LNP™ THERMOCOMP™ RF002 compound SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	36 kJ/m²
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	5.97 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	1.00 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	43 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	5.1 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	500 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ISO 178	4580 MPa
bending strength	bending strength	ASTM D790	189 MPa
bending strength	bending strength	bending strength	ISO 178	139 MPa
Tensile modulus	Tensile modulus	ASTM D638	5970 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	5240 MPa
tensile strength	tensile strength Break	ASTM D638	112 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2	90.0 MPa
elongation	elongation Break	ASTM D638	2.6 %
Tensile strain	Tensile strain Break	ISO 527-2	2.0 %
Bending modulus	Bending modulus	ASTM D790	5380 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	265 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	250 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	235 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	4.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	4.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	8.1E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.22 g/cm³
density	density	density	ISO 1183	1.21 g/cm³
Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.80 %
	Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	1.2 %
		Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	1.2 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.76 %
Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.80 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.7 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.