K(Q)胶 3G46 BASF GERMANY

So sánh
Xem giá

Bảng thông số kỹ thuật

optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
turbidity	turbidity	ASTM D1003	0.20 %
Refractive index	Refractive index	ASTM D542	1.573
Refractive index	Refractive index	Refractive index	ISO 489	1.573
transmissivity	transmissivity 550nm	ASTM D1003	91.0 %

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	3.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	32 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/A	2.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	3.0 kJ/m²
InstrumentedDartImpact	InstrumentedDartImpact Totalenergy	ASTM D3763	20.1 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	1640 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2	1550 Mpa
tensile strength	tensile strength Yield,23°C	ASTM D638	25.5 Mpa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2	27.0 Mpa
Tensile strain	Tensile strain Yield,23°C	ISO 527-2	2.0 %
elongation	elongation Break	ASTM D638	220 %
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2	180 %
Bending modulus	Bending modulus	ASTM D790	1330 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	1550 Mpa
bending strength	bending strength	ASTM D790	27.2 Mpa
	bending strength	bending strength 5.0%Strain		31.0 Mpa
	bending strength	bending strength	bending strength --	ISO 178	31.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	75.6 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	75.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	60.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	58.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15253	87.8 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	81.0 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	51.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	1.3E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	6.0E-5to9.0E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.02 g/cm³
density	density	density	ISO 1183	1.02 g/cm³
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTM D1238	11 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 200°C/5.0kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.65 %
Shrinkage rate	Shrinkage rate	Shrinkage rate	ISO 294-4	0.30-1.0 %
Water absorption rate	Water absorption rate Saturation,23°C	ASTM D570	0.070 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.070 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	>1.0E+14 ohms
Surface resistivity	Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms
Volume resistivity	Volume resistivity	ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric constant	Dielectric constant 1.00mm,1MHz	ASTM D150	2.50
Dielectric constant	Dielectric constant	Dielectric constant 100Hz	IEC 60250	2.50
Dissipation factor	Dissipation factor 100Hz	IEC 60250	3E-04
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	8E-04
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD	ASTM D2240	75
Shore hardness	Shore hardness ShoreD	ISO 868	65

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD

ASTM D2240

Shore hardness

ShoreD

ISO 868

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ISO 527-3	180 %

film

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

elongation

Break

ISO 527-3

180 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.