impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	22 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	180 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	59 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -18°C	ASTM D256	100 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	300 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/A	8.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	26 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2	2300 Mpa
tensile strength	tensile strength Yield,23°C	ASTM D638	45.0 Mpa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2	45.0 Mpa
Tensile strain	Tensile strain Yield,23°C	ISO 527-2	2.6 %
elongation	elongation Break	ASTM D638	2.6 %
Nominal tensile fracture strain	Nominal tensile fracture strain 23°C	ISO 527-2	10 %
Bending modulus	Bending modulus	ASTM D790	2300 Mpa
bending strength	bending strength	ASTM D790	65.0 Mpa
bending strength	bending strength	bending strength	ISO 178	65.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	8.0E-5to1.1E-4 cm/cm/°C
thermal conductivity	thermal conductivity	DIN 52612	0.17 W/m/K
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	90.6 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ASTM D648	104 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	99.0 °C
			Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	77.8 °C
				Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	98.9 °C
				Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	94.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	105 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.22 %
density	density	ASTM D792	1.04 g/cm³
density	density	density	ISO 1183	1.04 g/cm³
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTM D1238	1.5 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	19 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 230°C/3.8kg	ASTM D1238	4.80 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.40-0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate	ISO 294-4	0.40-0.70 %
Water absorption rate	Water absorption rate Saturation,23°C	ASTM D570	1.0 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	1.0 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms
Volume resistivity	Volume resistivity	ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Dielectric constant	Dielectric constant 1.00mm,1MHz	ASTM D150	2.80
Relative permittivity	Relative permittivity 100Hz	IEC 60250	2.90
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	2.80
Dissipation factor	Dissipation factor 100Hz	IEC 60250	4.8E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	7.9E-03

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	103
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	97.0 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

103

Ball Pressure Test

ISO 2039-1

97.0 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.