impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	50 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	6.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	8.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --	ISO 527-2	24000 Mpa
	Tensile modulus	Tensile modulus 120°C	ISO 527-2	10000 Mpa
		Tensile modulus	Tensile modulus 160°C	ISO 527-2	8800 Mpa
		Tensile modulus	Tensile modulus	Tensile modulus 180°C	ISO 527-2	8300 Mpa
tensile strength	tensile strength Break	ISO 527-2	240 Mpa
	tensile strength	tensile strength Break, 120°C	ISO 527-2	125 Mpa
		tensile strength	tensile strength Break, 160°C	ISO 527-2	105 Mpa
		tensile strength	tensile strength	tensile strength Break, 180°C	ISO 527-2	95.0 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	2.0 %
	Tensile strain	Tensile strain Break, 120°C	ISO 527-2	3.0 %
		Tensile strain	Tensile strain Break, 160°C	ISO 527-2	3.0 %
		Tensile strain	Tensile strain	Tensile strain Break, 180°C	ISO 527-2	3.0 %
Bending modulus	Bending modulus	ISO 178	18500 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Melting temperature	Melting temperature	ISO 11357-3	295 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	8.0E-6 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	3.4E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.28 g/cm³
Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow	ISO 294-4	0.20 %
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	2.6 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1.0E+2 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1.0E+2 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.