ABS Generic ABS+PC - Glass Fiber Generic
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 6.9to10 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179 | 25to40 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 58to130 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 4.0to14 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ASTM D256 | 310to800 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180 | 21to38 kJ/m² |
| Dart impact | Dart impact 23°C | ASTM D3763 | 13.3to35.0 J |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot filament ignition temperature | Hot filament ignition temperature | IEC 60695-2-13 | 642to755 °C |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus 23°C | ASTM D638 | 3450to9650 MPa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2 | 3300to7800 MPa |
| bending strength | bending strength 23°C | ASTM D790 | 94.3to173 MPa |
| bending strength | bending strength 23°C | ISO 178 | 92.3to144 MPa |
| bending strength | bending strength Yield,23°C | ASTM D790 | 101to138 MPa |
| bending strength | bending strength Break,23°C | ASTM D790 | 99.7to142 MPa |
| tensile strength | tensile strength Yield,23°C | ASTM D638 | 58.3to125 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2 | 58.3to95.6 MPa |
| tensile strength | tensile strength Break,23°C | ASTM D638 | 48.8to110 MPa |
| tensile strength | tensile strength Break,23°C | ISO 527-2 | 50.9to95.1 MPa |
| tensile strength | tensile strength 23°C | ASTM D638 | 73.1to125 MPa |
| elongation | elongation Yield,23°C | ASTM D638 | 2.5to5.0 % |
| elongation | elongation Yield,23°C | ISO 527-2 | 2.1to5.5 % |
| elongation | elongation Break,23°C | ASTM D638 | 1.5to7.4 % |
| elongation | elongation Break,23°C | ISO 527-2 | 2.0to5.1 % |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 2450to8580 MPa |
| Bending modulus | Bending modulus 23°C | ISO 178 | 3000to8230 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ASTME831 | 3.2E-5到7.3E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ISO 11359-2 | 7.9E-5到8.3E-5 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ASTM D648 | 92.0to139 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 89.0to140 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ASTM D648 | 87.5to136 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 112to124 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D1525 | 101to144 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306 | 99.4to140 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD | ASTM D696 | 6.5E-5到8.2E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ASTM D696 | 2.9E-5到6.1E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ASTME831 | 2.9E-5到7.7E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD | ISO 11359-2 | 1.7E-5到7.7E-5 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate 23°C | ISO 294-4 | 0.20to0.46 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ASTM D570 | 0.098to0.10 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.29to0.60 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.20to0.25 % |
| density | density -- | ASTM D792 | 1.17to1.43 g/cm³ |
| density | density 23°C | ISO 1183 | 1.17to1.43 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 250°C/2.16kg | ASTM D1238 | 2.3to4.1 g/10min |
| melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | ISO 1133 | 9.7to30 g/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/5.0kg | ISO 1133 | 14.8to20.0 cm³/10min |
| Shrinkage rate | Shrinkage rate MD:23°C | ASTM D955 | 0.15to0.43 % |
| Shrinkage rate | Shrinkage rate TD:23°C | ASTM D955 | 0.25to0.65 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity -- | ASTM D257 | 1.0E+2到2.5E+14 ohms |
| Surface resistivity | Surface resistivity -- | IEC 60093 | 9.8E+14到1.0E+15 ohms |
| Volume resistivity | Volume resistivity 23°C | ASTM D257 | 5.1E+5到1.3E+16 ohms·cm |
| Volume resistivity | Volume resistivity 23°C | IEC 60093 | 1.0E+13到1.0E+15 ohms·cm |
| Dielectric strength | Dielectric strength 23°C | ASTM D149 | 26to36 kV/mm |
| Arc resistance | Arc resistance | ASTM D495 | 69.0to106 sec |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 2 |
| High arc combustion index | High arc combustion index HAI | UL 746 | PLC 0 |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 4 mm/min |
| Hot wire ignition | Hot wire ignition HWI | UL 746 | PLC 0 sec |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness 23°C | ASTM D785 | 111to120 |