mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	3000 Mpa
Bending modulus	Bending modulus	ISO 178	2900 Mpa
Tensile creep modulus	Tensile creep modulus 1000 hr	ISO 899-1	-- Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2/50	25 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	4.4 %
tensile strength	tensile strength Yield	ISO 527-2/50	85.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	80 °C
drying time	drying time	4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.15 %
Hopper temperature	Hopper temperature	80 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	290 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	290 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	290 °C
Spray nozzle temperature	Spray nozzle temperature	290 °C
Processing (melt) temperature	Processing (melt) temperature	280 to 300 °C
Mold temperature	Mold temperature	60 to 80 °C
Residence Time	Residence Time	< 10.0 min
Screw speed	Screw speed	< 18 m/min

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Maximum operating temperature	Maximum operating temperature 短周期操作		200 °C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength --6	IEC 60216	121 °C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength --5	IEC 60216	147 °C
thermal conductivity	thermal conductivity	DIN 52612	0.33 W/m/K
specific heat	specific heat		1700 J/kg/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion 23 to 80°C，Flow	ISO 11359-2	7.0E-5 - 1.0E-4 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	260 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	75.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Mold Shrinkage - Constrained	Mold Shrinkage - Constrained		0.85 %
Stickiness	Stickiness 96% H2SO4	ISO 307	150 cm³/g
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	2.5 to 3.1 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	8.0 to 9.0 %
Shrinkage rate	Shrinkage rate Flow	ISO 294-4	1.4 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	1.7 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 275°C/5.0 kg	ISO 1133	100 cm3/10min
Apparent density	Apparent density		0.70 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	-- ohms
Volume resistivity	Volume resistivity	IEC 60093	1.0E+15 ohms·cm
Relative permittivity	Relative permittivity 1 MHz	IEC 60250	3.20
Dissipation factor	Dissipation factor 1 MHz	IEC 60250	0.025
Compared to the anti leakage trace index	Compared to the anti leakage trace index Solution A	IEC 60112	V

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.