PA6 K224-G0 DSM Additive Manufacturing

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	95 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	15 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	725 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	725 °C
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	700 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	700 °C
UL flame retardant rating	UL flame retardant rating 3.0mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	310 MPa
Bending modulus	Bending modulus	ISO 178	13000 MPa
Tensile strain	Tensile strain Break	ISO 527-2	3.0 %
Tensile modulus	Tensile modulus	ISO 527-2	16500 MPa
tensile strength	tensile strength Break	ISO 527-2	220 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	220 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	210 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.56 g/cm³
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.76 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.33 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	4.5 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.4 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V
Dielectric strength	Dielectric strength	IEC 60243-1	35 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	-- ohms
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.015
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	5E-03
Relative permittivity	Relative permittivity 1MHz	IEC 60250	5.20
Relative permittivity	Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.50

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.