mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield,23°C	ASTM D638	71.7 MPa
elongation	elongation Break,23°C	ASTM D638	2.5 %
Bending modulus	Bending modulus 23°C	ASTM D790	3870 MPa
bending strength	bending strength Yield,23°C	ASTM D790	123 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	96.7 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	85.6 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15252	108 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	5.9E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.30to0.70 %
density	density	ASTM D792	1.07 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/3.8kg	ASTM D1238	8.0 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ASTM D955

0.30to0.70 %

density

ASTM D792

1.07 g/cm³

melt mass-flow rate

230°C/3.8kg

ASTM D1238

8.0 g/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	125

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

125

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.