mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	Internal Method	221 MPa
bending strength	bending strength	Internal Method	414 MPa
Poisson's ratio	Poisson's ratio	ASTM D3039	0.17

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

tensile strength

Internal Method

221 MPa

bending strength

Internal Method

414 MPa

Poisson's ratio

ASTM D3039

0.17

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Glass transition temperature	Glass transition temperature	Internal Method	200 °C
thermal conductivity	thermal conductivity 100°C	ASTME1461	0.30 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：>200°C7	Internal Method	1.6E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：<200°C7	Internal Method	5.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：--6	Internal Method	1.7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr	Internal Method	<1.0 %
decomposition temperature	decomposition temperature 5%	Internal Method	330 °C
decomposition temperature	decomposition temperature Intial	Internal Method	311 °C

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Water absorption rate

24hr

Internal Method

<1.0 %

decomposition temperature

Internal Method

330 °C

decomposition temperature

Intial

Internal Method

311 °C

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	Internal Method	0.010
Arc resistance	Arc resistance	Internal Method	125 sec
Dielectric constant	Dielectric constant 1MHz	Internal Method	4.25
Dielectric strength	Dielectric strength	Internal Method	63 kV/mm
Volume resistivity	Volume resistivity --9	Internal Method	4.7E+15 ohms·cm
Volume resistivity	Volume resistivity	Volume resistivity --8	Internal Method	8.2E+13 ohms·cm
Surface resistivity	Surface resistivity --9	Internal Method	1.2E+15 ohms
Surface resistivity	Surface resistivity	Surface resistivity --8	Internal Method	4.4E+12 ohms

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Peel strength	Peel strength --3	Internal Method	1.5 kN/m
Peel strength	Peel strength toKapton4	Internal Method	1.0 kN/m
Peel strength	Peel strength toKapton5	Internal Method	0.9 kN/m

film

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Peel strength

--3

Internal Method

1.5 kN/m

Peel strength

toKapton4

Internal Method

1.0 kN/m

Peel strength

toKapton5

Internal Method

0.9 kN/m

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
expansion rate	expansion rate 50to260°C	Internal Method	1.5 %
t	t	Internal Method	50.0 min
	t	t	Internal Method	5.0 min
	t	t	t	Internal Method	3.0 min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.