mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --3	ASTM D638	2100 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/50	2100 Mpa
tensile strength	tensile strength Yield3	ASTM D638	64.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	65.0 Mpa
		tensile strength	tensile strength Break3	ASTM D638	64.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	65.0 Mpa
elongation	elongation Break3	ASTM D638	85 %
elongation	elongation	elongation Break	ISO 527-2/50	85 %
Bending modulus	Bending modulus --4	ASTM D790	2500 Mpa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	2400 Mpa
bending strength	bending strength --4	ASTM D790	93.0 Mpa
bending strength	bending strength	bending strength --5	ISO 178	90.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Hot air dryer	Hot air dryer	80 °C
Vacuum drying machine	Vacuum drying machine	80 °C
Hot air dryer	Hot air dryer	4.0 hr
Vacuum drying machine	Vacuum drying machine	4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	< 0.050 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 270 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	260 to 280 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	270 to 290 °C
Spray nozzle temperature	Spray nozzle temperature	270 to 290 °C
Mold temperature	Mold temperature	60 to 80 °C
Injection pressure	Injection pressure	98.1 Mpa
Back pressure	Back pressure	0.490 to 1.96 Mpa
Screw speed	Screw speed	50 to 150 rpm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	105 °C
	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	105 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	97.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	92.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	108 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 220°C/10.0 kg	ASTM D1238	20 g/10 min
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	ASTM D955	0.40 - 0.60 %
	Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.60 %
		Shrinkage rate	Shrinkage rate 横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.60 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 2.00 mm	ISO 294-4	0.40 - 0.60 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	119
Rockwell hardness	Rockwell hardness R -Sale	ISO 2039-2	119

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

119

Rockwell hardness

R -Sale

ISO 2039-2

119

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.