impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 30℃	ASTM D256	160 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D256	534 J/m
Instrumented dart impact energy -30 ℃ (-22 ℉) peak	Instrumented dart impact energy -30 ℃ (-22 ℉) peak	ASTM D3763	54 J
Instrumented dart impact energy 23 ℃ (73 ℉) total energy	Instrumented dart impact energy 23 ℃ (73 ℉) total energy	ASTM D3763	61 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Type I, 50，Yield	ASTM D638	62 Mpa
Elongation at Break	Elongation at Break Type I, 50	ASTM D638	40
bending strength	bending strength 2.6 mm/，Yield	ASTM D790	102 Mpa
Bending modulus	Bending modulus 2.6 mm/	ASTM D790	2650 Mpa

thermal properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature Rate B/50	ASTM D1525	85 °C
RTI Imp	RTI Imp	UL 746B	85 °C
RTI Elec	RTI Elec	UL 746B	85 °C
RTI Imp	RTI Imp	UL 746B	85 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -30°C to 3，Flow	ASTM E831	72 E-6/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -30°C to 3，Across Flow	ASTM E831	72 E-6/°C
thermal conductivity	thermal conductivity	ASTM C 177	0.2 W/m-°C

combustion performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL fire rating V	UL fire rating V	UL 94	1.5 mm
UL fire rating 5VB	UL fire rating 5VB	UL 94	2.49 mm
Limiting Oxygen Index (LOI)	Limiting Oxygen Index (LOI)	ASTM D 2863	32 %

combustion performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL fire rating V

UL 94

1.5 mm

UL fire rating 5VB

UL 94

2.49 mm

Limiting Oxygen Index (LOI)

ASTM D 2863

32 %

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate	ASTM D1238	10 g/10min
Shrinkage rate	Shrinkage rate flow, 3.2	Internal	0.4-0.8
Shrinkage rate	Shrinkage rate	Shrinkage rate xflow, 3.2	Internal	0.4-0.6
Water absorption rate	Water absorption rate flow, 3.2	ASTM D570	0.4
Water absorption rate	Water absorption rate	Water absorption rate 24 hours	ASTM D570	0.1

Electrical Property	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D257	100000000000000000 ohm-cm
Surface resistivity	Surface resistivity	ASTM D257	10000000000000000 Ohm
Dielectric constant	Dielectric constant	ASTM D 150	3
Dielectric constant	Dielectric constant	Dielectric constant	ASTM D 150	3
Dissipation factor	Dissipation factor	ASTM D 150	50 E-4
Dissipation factor	Dissipation factor	Dissipation factor	ASTM D 150	49 E-4
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	UL 746A	PLC_0
Dielectric strength	Dielectric strength in oil, 3.2	ASTM D149	19.5 kV/mm
Arc resistance	Arc resistance	ASTM D495	PLC_6
High voltage arc tracing rate	High voltage arc tracing rate	UL 746A	PLC 2
Hot wire ignition (HWI)	Hot wire ignition (HWI)	UL 746A	PLC_1
High current arc ignition (HAI)	High current arc ignition (HAI)	UL 746A	PLC_0

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hardness (Rockwell R)	Hardness (Rockwell R)	ASTM D785	123 R

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hardness (Rockwell R)

ASTM D785

123 R

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.