PBT+PET PBT/PET 28 GF30 Bada AG

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	55 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	10 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

UL flame retardant rating

0.8mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23°C	ISO 178	210 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.6 %
tensile strength	tensile strength Break,23°C	ISO 527-2/5	140 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	10000 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Maximum operating temperature	Maximum operating temperature somehours		160 °C
Maximum operating temperature	Maximum operating temperature	Maximum operating temperature 20000h	IEC 216	140 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	DIN 53752	9.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	DIN 53752	3.5E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 3146	235 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	202 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.55 g/cm³
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.37 %
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.18 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

23°C

ISO 1183

1.55 g/cm³

Water absorption rate

Saturation,23°C

ISO 62

0.37 %

Water absorption rate

Equilibrium,23°C,50%RH

ISO 62

0.18 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 2
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.017
Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.10
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+16 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+14 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.