impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	80 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 0.75mm	IEC 60695-2-13	825 °C
	Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	825 °C
	Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	850 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	33 %
Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 0.75mm	IEC 60695-2-12	960 °C
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94,IEC60695-11-10,-20	V-0
	UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94,IEC60695-11-10,-20	V-0
		UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94,IEC60695-11-10,-20	V-0
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 0.40mm	UL 94,IEC60695-11-10,-20	V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Yield	ISO 527-2/1A/50	35 %
Bending modulus	Bending modulus	ISO 178	2350 MPa
bending strength	bending strength 3.5%Strain	ISO 178	55.0 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A/50	50.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	2050 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	184 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	214 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	112 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	178 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 240°C/2.16kg	ISO 1133	5.00 cm³/10min
density	density	ISO 1183/A	1.25 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Melt Volume Flow Rate (MVR)

240°C/2.16kg

ISO 1133

5.00 cm³/10min

density

ISO 1183/A

1.25 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 0

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

CTI

UL 746

PLC 0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.