impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	79.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	9.0 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	6.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	990 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	200 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break	ISO 527-2/50	59.0 MPa
	tensile strength	tensile strength Break	ASTM D638	65.0 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	62.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	61.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	2660 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	2300 MPa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	96.0 MPa
bending strength	bending strength	bending strength	ISO 178	92.0 MPa
Bending modulus	Bending modulus	ISO 178	2190 MPa
elongation	elongation Yield	ASTM D638	6.0 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.4 %
elongation	elongation Break	ASTM D638	130 %
Tensile strain	Tensile strain Break	ISO 527-2/50	110 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2320 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	6.3E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	6E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	127 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	125 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D152510	125 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	105 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	104 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
OutdoorSuitability	OutdoorSuitability Natural	UL 746C	f1
density	density	ASTM D792	1.20 g/cm³
density	density	density	ISO 1183	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 265°C/2.16kg	ASTM D1238	8.0 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	5.00 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50to0.80 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.32 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.12 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.