DAP Synres-Almoco DAP 5567 Synres-Almoco BV
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch Compression Molded | ISO 179/1eU | 5.0to10 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength Injection | ISO 179/1eA | 3.5to5.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength Compression Molded | ISO 179/1eA | 2.5to3.5 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch Injection | ISO 179/1eU | 8.0to11 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot filament ignition temperature | Hot filament ignition temperature | IEC 60695-2-13 | 930 °C |
| Burning wire flammability index | Burning wire flammability index | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | UL flame retardant rating 0.8mm | UL 94 | V-0 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Injection | ISO 527-2 | 40.0to70.0 MPa |
| tensile strength | tensile strength CompressionMolded | ISO 527-2 | 35.0to60.0 MPa |
| Compressive stress | Compressive stress | ISO 604 | 150to200 MPa |
| bending strength | bending strength Injection | ISO 178 | 100to140 MPa |
| bending strength | bending strength Compression Molded | ISO 178 | 80.0to100 MPa |
| Bending modulus | Bending modulus Injection | ISO 178 | 13000to16000 MPa |
| Bending modulus | Bending modulus Compression Molded | ISO 178 | 8000to12000 MPa |
| Tensile modulus | Tensile modulus Compression Molded | ISO 527-2 | 6000to9000 MPa |
| Tensile modulus | Tensile modulus Injection | ISO 527-2 | 9000to11000 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| thermal conductivity | thermal conductivity | ASTME1461 | 0.90to1.1 W/m/K |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：50to100°C | ISO 11359-2 | 5.0E-6到1.0E-5 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 8.0MPa,Unannealed | ISO 75-2/C | >180 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | >200 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ISO 1183 | 1.90to2.10 g/cm³ |
| Apparent density | Apparent density | ISO 60 | 0.75to0.90 g/cm³ |
| Shrinkage rate | Shrinkage rate MD：--2 | ISO 2577 | 0.30to0.40 % |
| Shrinkage rate | Shrinkage rate MD：--3 | ISO 2577 | 0.50to0.60 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | <0.20 % |
| Shrinkage rate | Shrinkage rate | ISO 2577 | <0.050 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 4.004.50 |
| Dissipation factor | Dissipation factor 100Hz | IEC 60250 | 0.010to0.030 |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.010to0.030 |
| Relative permittivity | Relative permittivity 100Hz | IEC 60250 | 4.505.00 |
| Dielectric strength | Dielectric strength | IEC 60243-1 | 35to40 kV/mm |
| Volume resistivity | Volume resistivity | IEC 60093 | 1.0E+14到1.0E+15 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 1.0E+14到1.0E+15 ohms |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |
| Arc resistance | Arc resistance | ASTM D495 | PLC 4 |