impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ASTM D256	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -20°C	ISO 179	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C,4.00mm	ASTM D256	NoBreak
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C	ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C,4.00mm	ASTM D256	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	NoBreak
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180	8.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,4.00mm，Area	ASTM D256	NoBreak
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C,4.00mm，Area	ASTM D256	6.30 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ASTM D256	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ASTM D256	34 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	33 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179	13 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ASTM D256	13 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ASTM D638	17.9 MPa
	tensile strength	tensile strength Yield	ASTM D638	26.2 MPa
		tensile strength	tensile strength Yield	ISO 527-2	26.0 MPa
		tensile strength	tensile strength	tensile strength 4.00mm	ISO 527-2	18.0 MPa
elongation	elongation Yield	ASTM D638	10 %
Tensile strain	Tensile strain Yield	ISO 527-2	10 %
Bending modulus	Bending modulus 4.00mm	ISO 178	1300 MPa
Bending modulus	Bending modulus	Bending modulus 4.00mm	ASTM D790	1300 MPa
Tensile strain	Tensile strain Break,4.00mm	ISO 527-2	30 %
elongation	elongation Break	ASTM D638	30 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648B	80.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	80.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/A50	150 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D15253	149 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	52.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648A	52.2 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.02 g/cm³
density	density	density	ISO 1183	1.02 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	3.5 g/10min
Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.2to1.8 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ASTM D955	1.2to1.8 %
melt mass-flow rate	melt mass-flow rate 230°C/5.0kg	ISO 1133	21 g/10min
	melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	3.5 g/10min
	melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 230°C/5.0kg	ASTM D1238	21 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ESDSTM11.11	<1.0E+4 ohms
Surface resistivity	Surface resistivity	IEC 61340-2-3	<1.0E+4 ohms
Volume resistivity	Volume resistivity	Internal Method	<1.0E+3 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ESDSTM11.11

<1.0E+4 ohms

Surface resistivity

IEC 61340-2-3

<1.0E+4 ohms

Volume resistivity

Internal Method

<1.0E+3 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA	ASTM D2240	96
	Shore hardness	Shore hardness ShoreD	ASTM D2240	71
		Shore hardness	Shore hardness ShoreA	ISO 868	96
		Shore hardness	Shore hardness	Shore hardness ShoreD	ISO 868	71

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.