flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.1mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	875 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	35 %
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	V-2

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	101 Mpa
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2340 Mpa
elongation	elongation Break	ASTM D638	130 %
elongation	elongation	elongation Yield	ASTM D638	6.0 %
tensile strength	tensile strength Break	ASTM D638	65.5 Mpa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	62.1 Mpa
Tensile modulus	Tensile modulus	ASTM D638	2280 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Str	RTI Str	UL 746	130 °C
RTI Imp	RTI Imp	UL 746	120 °C
RTI Elec	RTI Elec	UL 746	130 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	143 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	127 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	138 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.60-0.80 %
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	10 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

MD：3.20mm

Internal Method

0.60-0.80 %

melt mass-flow rate

300°C/1.2kg

ASTM D1238

10 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 2
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 4
High arc combustion index	High arc combustion index HAI	UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 2
Arc resistance	Arc resistance	ASTM D495	PLC7

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.