HMW-HDPE L5008 HMC Polymers

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Fundamentals of Hydrostatic Design	Fundamentals of Hydrostatic Design 60°C	ASTM D2837	6.89 MPa
Fundamentals of Hydrostatic Design	Fundamentals of Hydrostatic Design	Fundamentals of Hydrostatic Design 23°C	ASTM D2837	11.0 MPa
Bending modulus	Bending modulus	ASTM D790	972 MPa
elongation	elongation Break	ASTM D638	640 %
tensile strength	tensile strength Break	ASTM D638	34.3 MPa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	24.4 MPa
melt mass-flow rate	melt mass-flow rate 190°C/21.6kg	ASTM D1238	16 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	0.070 g/10min
density	density	ASTM D1505	0.949 g/cm³
Slow Crack Growth (PENT)	Slow Crack Growth (PENT) 80°C	ASTMF1473	>100 hr
DSCInductionTemperature	DSCInductionTemperature	ASTM D3350	267 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	68.0 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.