PPO(PPE)+PS+PP Generic PPE+PS+PP Generic

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C	ASTM D3763	36.2to45.9 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	150to590 J/m

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dart impact

23°C

ASTM D3763

36.2to45.9 J

Impact strength of cantilever beam gap

23°C

ASTM D256

150to590 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield,23°C	ASTM D638	33.8to43.8 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	1660to1760 MPa
Tensile modulus	Tensile modulus	Tensile modulus 23°C	ASTM D638	1170to1710 MPa
bending strength	bending strength Yield,23°C	ASTM D790	49.0to53.2 MPa
Bending modulus	Bending modulus 23°C	ASTM D790	1340to1560 MPa
elongation	elongation Break,23°C	ISO 527-2	46to120 %
	elongation	elongation Break,23°C	ASTM D638	83to200 %
	elongation	elongation	elongation Yield,23°C	ASTM D638	6.5to15 %
tensile strength	tensile strength Break,23°C	ASTM D638	27.6to41.5 MPa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2	33.9to44.6 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ASTME831	7.2E-5到1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTME831	8.1E-5到1.6E-4 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306	102to118 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D1525	85.0to146 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	71.1to92.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	110to113 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD：23°C	ASTM D955	0.65to1.0 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	11to16 g/10min
density	density	ASTM D792	0.987to1.03 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

MD：23°C

ASTM D955

0.65to1.0 %

melt mass-flow rate

260°C/5.0kg

ASTM D1238

11to16 g/10min

density

ASTM D792

0.987to1.03 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.