PPO(PPE)+SEBS LNP™ THERMOCOMP™ ZKC04 compound SABIC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C8 | ISO 180/1A | 55 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C | ASTM D256 | 140 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 720 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C8 | ISO 180/1A | 13 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 1.030mm | UL 94 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus --2 | ASTM D638 | 2290 MPa |
| Tensile modulus | Tensile modulus -- | ISO 527-2/1 | 2240 MPa |
| tensile strength | tensile strength Yield3 | ASTM D638 | 58.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 57.0 MPa |
| tensile strength | tensile strength Break3 | ASTM D638 | 51.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2/50 | 49.0 MPa |
| elongation | elongation Yield3 | ASTM D638 | 9.0 % |
| elongation | elongation Yield | ISO 527-2/50 | 8.9 % |
| elongation | elongation Break3 | ASTM D638 | 34 % |
| elongation | elongation Break | ISO 527-2/50 | 33 % |
| Bending modulus | Bending modulus 50.0mmSpan4 | ASTM D790 | 2080 MPa |
| Bending modulus | Bending modulus --5 | ISO 178 | 2210 MPa |
| bending strength | bending strength --5,6 | ISO 178 | 93.0 MPa |
| bending strength | bending strength --5,7 | ISO 178 | 91.0 MPa |
| bending strength | bending strength Yield,50.0mmSpan4 | ASTM D790 | 86.0 MPa |
| bending strength | bending strength Break,50.0mmSpan4 | ASTM D790 | 84.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,3.20mm | ASTM D648 | 174 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan9 | ISO 75-2/Bf | 175 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 154 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan9 | ISO 75-2/Af | 155 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to150°C | ASTME831 | 6.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to150°C | ASTME831 | 9.4E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| melt mass-flow rate | melt mass-flow rate 300°C/10.0kg | ASTM D1238 | 33 g/10min |
| melt mass-flow rate | melt mass-flow rate 300°C/5.0kg | ASTM D1238 | 11 g/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/10.0kg | ISO 1133 | 31.0 cm³/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/5.0kg | ISO 1133 | 10.0 cm³/10min |
| Shrinkage rate | Shrinkage rate TD:24hr | ISO 294-4 | 0.70to0.90 % |
| Shrinkage rate | Shrinkage rate MD:24hr | ISO 294-4 | 0.70to0.90 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.050 % |
| density | density | ISO 1183 | 1.21 g/cm³ |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dielectric constant | Dielectric constant 10.0GHz | Internal Method | 3.06 |
| Dissipation factor | Dissipation factor 1.10GHz | Internal Method | 9E-04 |
| Dissipation factor | Dissipation factor 1.90GHz | Internal Method | 1.1E-03 |
| Dissipation factor | Dissipation factor 5.00GHz | Internal Method | 1.4E-03 |
| Dissipation factor | Dissipation factor 10.0GHz | Internal Method | 2E-03 |
| Dielectric constant | Dielectric constant 1.10GHz | Internal Method | 3.04 |
| Dielectric constant | Dielectric constant 1.90GHz | Internal Method | 3.05 |
| Dielectric constant | Dielectric constant 5.00GHz | Internal Method | 3.06 |