flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 2.0mm	UL 94	5VB5VA
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	825 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ISO 527-2/5	88.0 Mpa
	tensile strength	tensile strength Break4	ASTM D638	88.0 Mpa
	tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	88.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/5	3.0 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/5	3.0 %
Bending modulus	Bending modulus 50.0mmSpan5	ASTM D790	4600 Mpa
Bending modulus	Bending modulus	Bending modulus --6	ISO 178	4600 Mpa
bending strength	bending strength --6,7	ISO 178	145 Mpa
bending strength	bending strength	bending strength Yield,50.0mmSpan5	ASTM D790	145 Mpa
Tensile modulus	Tensile modulus --3	ASTM D638	5000 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	5000 Mpa
tensile strength	tensile strength Yield4	ASTM D638	88.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	220 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan10	ISO 75-2/Bf	224 °C
Vicat softening temperature	Vicat softening temperature --	ASTMD152511	218 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	220 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	4.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	7.4E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	18 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	Shrinkage rate MD:3.20mm	Internal Method	0.88-0.94 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:3.20mm	Internal Method	0.95-1.0 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	3.8 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.50 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D257	1E+16 ohms·cm
Dielectric strength	Dielectric strength 1.60mm,inAir	ASTM D149	23 KV/mm
Dielectric strength	Dielectric strength	Dielectric strength 1.60mm,inOil	ASTM D149	24 KV/mm
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 1
High arc combustion index	High arc combustion index HAI	UL 746	PLC 0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.