PC+PET Infino AE-2130 LOTTE KOREA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	38 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	33 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	550 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	180 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ASTM D790	81.0 MPa
bending strength	bending strength	bending strength	ISO 178	82.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	2300 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/50	2400 MPa
tensile strength	tensile strength Yield	ASTM D638	57.0 MPa
	tensile strength	tensile strength Yield	ISO 527-2/50	56.0 MPa
		tensile strength	tensile strength Break	ASTM D638	56.0 MPa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	55.0 MPa
elongation	elongation Break	ASTM D638	90 %
Tensile strain	Tensile strain Break	ISO 527-2/50	90 %
Bending modulus	Bending modulus	ASTM D790	2500 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2400 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	128 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ISO 75-2/B	120 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed,4.00mm	ISO 75-2/B	125 °C
			Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	108 °C
				Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	98.0 °C
				Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed,4.00mm	ISO 75-2/A	112 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	132 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.23 g/cm³
density	density	density	ISO 1183	1.23 g/cm³
melt mass-flow rate	melt mass-flow rate 250°C/2.16kg	ASTM D1238	2.8 g/10min
	melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	21 g/10min
		melt mass-flow rate	melt mass-flow rate 250°C/2.16kg	ISO 1133	2.8 g/10min
		melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ISO 1133	21 g/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.30to0.50 %
	Shrinkage rate	Shrinkage rate TD：3.20mm	ASTM D955	0.30to0.50 %
		Shrinkage rate	Shrinkage rate TD:3.20mm	ISO 2577	0.30to0.50 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:3.20mm	ISO 2577	0.30to0.50 %
ash content	ash content --	ISO 3451	4.0 %
ash content	ash content	ash content --	ASTM D5630	4.0 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	111
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	111

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

111

Rockwell hardness

R-Scale

ISO 2039-2

111

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.