| Vicat softening temperature | Vicat softening temperature | °C | 105 -- |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | °C | 89.0 -- |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | | 无断裂 -- |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | | 无断裂 -- |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | kJ/m² | 60 -- |
| Tensile modulus | Tensile modulus 23°C | MPa | 1700 1200 |
| Water absorption rate | Water absorption rate 23°C,24hr | % | 1.0 -- |
| Shrinkage rate | Shrinkage rate 23°C | % | 0.60to0.90 -- |
| melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | g/10min | 15 -- |
| density | density 23°C | g/cm³ | 1.06 -- |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | kJ/m² | 11 -- |
| bending strength | bending strength 23°C | MPa | 58.0 -- |
| Tensile strain | Tensile strain Break,23°C | % | >100 >200 |
| thermal conductivity | thermal conductivity | W/m/K | 0.25 -- |
| tensile strength | tensile strength 23°C | MPa | 37.0 34.0 |