machinability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dry conditions	Dry conditions		160℃3H
Processing temperature	Processing temperature		290-300 °C
	Processing temperature	Processing temperature		310 °C
		Processing temperature	Processing temperature		300 °C
		Processing temperature	Processing temperature	Processing temperature		310-320 °C
Mold temperature	Mold temperature		150 °C

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	V-0

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL 94

V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ASTM D638/ISO 527	185 kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	ASTM D790/ISO 178	13000 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	260 kg/cm²(MPa)[Lb/in²]
Elongation at Break	Elongation at Break	ASTM D638/ISO 527	1.8 %
tensile strength	tensile strength	ISO 527-2	185 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	1.8 %
Bending modulus	Bending modulus	ISO 178	1300 Mpa
bending strength	bending strength	ISO 178	260 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility (rate)	Combustibility (rate)	UL 94	V-0
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D696/ISO 11359	- mm/mm.℃
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	265 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	Internal Method	1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	Internal Method	4E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792/ISO 1183	1.66
Water absorption rate	Water absorption rate	ASTM D570/ISO 62	0.01 %
Water absorption rate	Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.030 %
Melt viscosity	Melt viscosity 310°C,1000sec^-1	ISO 11443	380000 mPa·s

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	ASTM D257/IEC 60093	1.0 x 10^16 Ω.cm
Volume resistivity	Volume resistivity	Volume resistivity	IEC 60093	1E+16 ohms·cm
Dielectric strength	Dielectric strength 3.00mm	IEC 60243-1	15 KV/mm
Relative permittivity	Relative permittivity 1kHz	IEC 60250	4.60
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.60
Dissipation factor	Dissipation factor 1kHz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor 1MHz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor	Dissipation factor 耐电弧性	IEC 60250	120 sec
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Scale	ISO 2039-2	105

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Scale

ISO 2039-2

105

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ColourNumber	ColourNumber		HF2000/HD9050

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ColourNumber

HF2000/HD9050

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.