PPS+PPE NORYL™ APS130 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	88 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	88 J/m

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of cantilever beam gap

23°C

ASTM D256

88 J/m

Impact strength of cantilever beam gap

23°C

ASTM D256

88 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	Internal Method	113 MPa
bending strength	bending strength	ASTM D790	157 MPa
Bending modulus	Bending modulus	ASTM D790	8430 MPa
bending strength	bending strength	ASTM D790	157 MPa
Bending modulus	Bending modulus	ASTM D790	8430 MPa
elongation	elongation Break	Internal Method	8.0 %
elongation	elongation	elongation Break	Internal Method	8.0 %
tensile strength	tensile strength Yield	Internal Method	113 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTME831	2.5E-5到5.5E-5 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	267 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	267 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTME831	2.5E-5到5.5E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.020 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.25to0.70 %
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	29 g/10min
density	density	ASTM D792	1.44 g/cm³
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.020 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.25to0.70 %
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	29 g/10min
density	density	ASTM D792	1.44 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.30
Dielectric constant	Dielectric constant	Dielectric constant 50Hz	ASTM D150	3.30
Dielectric strength	Dielectric strength 1.60mm,inOil	ASTM D149	22 kV/mm
Surface resistivity	Surface resistivity	ASTM D257	1E+16 ohms
Surface resistivity	Surface resistivity	Surface resistivity	ASTM D257	1E+16 ohms
Dielectric strength	Dielectric strength 1.60mm,inOil	ASTM D149	22 kV/mm
Dielectric constant	Dielectric constant 50Hz	ASTM D150	3.30
Dielectric constant	Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.30

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.