PC LEXAN™ HP1R-1H112 SABIC INNOVATIVE CANADA

230

Đặc tính:
Dòng chảy cao
Lĩnh vực ứng dụng:
Chăm sóc y tếThuốcVật tư y tế/điều dưỡng
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	54.0 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus 50.0mmSpan5	ASTM D790	2300 Mpa
Bending modulus	Bending modulus	Bending modulus --6	ISO 178	2300 Mpa
bending strength	bending strength --6,7	ISO 178	90.0 Mpa
bending strength	bending strength	bending strength Yield,50.0mmSpan5	ASTM D790	93.0 Mpa
Tensile modulus	Tensile modulus --3	ASTM D638	2370 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2350 Mpa
tensile strength	tensile strength Yield4	ASTM D638	62.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	63.0 Mpa
		tensile strength	tensile strength Break4	ASTM D638	65.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	50.0 Mpa
elongation	elongation Yield4	ASTM D638	6.0 %
	elongation	elongation Yield	ISO 527-2/50	6.0 %
		elongation	elongation Break4	ASTM D638	120 %
		elongation	elongation	elongation Break	ISO 527-2/50	70 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	126 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan10	ISO 75-2/Ae	121 °C
Vicat softening temperature	Vicat softening temperature --	ASTMD152511	139 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	140 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to95°C	ASTME831	6.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to80°C	ISO 11359-2	7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to95°C	ASTME831	6.8E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	28 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 1133	26.0 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.15 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.