Polyolefin, Enhanced TPO POLYTROPE® STR 2031REU-01 NATURAL A SCHULMAN USA

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break,233°C	ISO 527-2	550 %
tensile strength	tensile strength Yield,23°C	ISO 527-2	21.4 MPa
Shrinkage rate	Shrinkage rate 23°C,24hr,3.18mm	ISO 294-4	0.90to1.3 %
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	0.80 g/10min
density	density	ISO 1183	1.18 g/cm³
HeatSag	HeatSag 149°C,3.20mm	ASTM D3769	0.00 mm
gloss	gloss 60°,3180μm,热塑,光滑	ISO 2813	20to40
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to100°C	ASTME831	5.6E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	87.8 °C
Dart impact	Dart impact -20°C,TotalEnergy,韧性破坏	ASTM D3763	46.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm,Injection，Flow	ASTM D256	680 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C,3.18mm,Injection，Flow	ASTM D256	53 J/m
Bending modulus	Bending modulus 23°C	ISO 178	1790 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.