HDPE PRE-ELEC® TP 11270 Premix Oy
--
--
--
- -
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Thông số kỹ thuật

impact performanceĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
Suspended wall beam without notch impact strength-20°CISO 180无断裂
Charpy Notched Impact Strength23°CASTM D25613 kJ/m²
Impact strength of cantilever beam gap-20°C,4.00mmASTM D2564.20 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D256无断裂
Impact strength of cantilever beam gap-20°CISO 1805.0 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180无断裂
Charpy Notched Impact Strength-20°CISO 1794.0 kJ/m²
Impact strength of cantilever beam gap23°C,4.00mmASTM D25612.6 kJ/m²
Impact strength of simply supported beam without notch-20°CISO 179无断裂
Impact strength of cantilever beam gap23°CISO 18013 kJ/m²
Charpy Notched Impact Strength23°CISO 17912 kJ/m²
-20°CASTM D2564.2 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179无断裂
Suspended wall beam without notch impact strength23°C,4.00mmASTM D256无断裂
mechanical propertiesĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
elongationFlow:BreakASTM D638>600 %
tensile strengthFlow:YieldISO 527-225.0 MPa
elongationFlow:YieldASTMD63826 %
tensile strength4.00mm3ISO 527-227.0 MPa
4.00mm2ISO 527-246.0 MPa
FlowASTM D63846.2 MPa
Bending modulus4.00mmASTMD7901200 MPa
tensile strengthFlow:YieldASTM D63824.8 MPa
横向Flow:YieldISO 527-225.0 MPa
elongationBreak,0.400mm3ISO 527-2>600 %
tensile strength横向FlowASTM D63826.2 MPa
横向Flow:YieldASTM D63824.8 MPa
elongation横向Flow:YieldASTMD6388.0 %
Break,4.00mm2ISO 527-2>600 %
横向Flow:BreakASTM D638>600 %
thermal performanceĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
Hot deformation temperature1.8MPa,UnannealedISO 75-2/Af45.0 °C
Vicat softening temperature--ISO 306/B5087.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/Bf76.0 °C
1.8MPa,UnannealedASTM D648A47.8 °C
Vicat softening temperature--ASTMD15256127 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648B82.2 °C
Vicat softening temperature--ASTM D1525560.0 °C
Physical propertiesĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
Shrinkage rateMDISO 294-42.5to3.5 %
MDASTM D9552.5to3.5 %
melt mass-flow rate190°C/21.6kgASTMD123815 g/10min
density--ISO 11831.03 g/cm³
--ASTM D7921.05 g/cm³
Electrical performanceĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
Volume resistivityInternal Method<1.0E+4 ohms·cm
Surface resistivityESDSTM11.11,IEC61340-2-3<1.0E+5 ohms
hardnessĐiều kiện kiểm traPhương pháp kiểm traPremix Oy/PRE-ELEC® TP 11270
Shore hardnessShoreDASTMD224070
ShoreAASTMD224097