mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Oxford Performance Materials, Inc./OXPEKK® MG240C
Bending modulus		ASTM D790	3000 MPa
compressive strength		ASTM D695	241 MPa
tensile strength	Break	ASTM D638	269 MPa
Tensile modulus		ASTM D638	3500 MPa
bending strength		ASTM D790	300 MPa
elongation	Break	ASTM D638	1.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Oxford Performance Materials, Inc./OXPEKK® MG240C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	327 °C
Melting temperature		DSC	360 °C
Linear coefficient of thermal expansion	MD	ASTM D696	1.1E-05 cm/cm/°C
Glass transition temperature		DSC	163 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Oxford Performance Materials, Inc./OXPEKK® MG240C
Shrinkage rate	MD	ASTM D955	0.050 %
Water absorption rate	24hr	ASTM D570	<0.030 %
density		ASTM D792	1.47 g/cm³