So sánh vật liệu
Thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm,Injection | ASTM D256A | 27 J/m |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
| 1.5mm | IEC 60695-2-13 | 960 °C | |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 960 °C |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| Bending modulus | ASTM D790 | 1100 MPa | |
| Poisson's ratio | ASTM D638 | 0.43 | |
| tensile strength | Yield | ASTM D638 | 28.3 MPa |
| elongation | Break | ASTM D638 | 230 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.18mm | ASTM D648 | 90.0 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 4.0to12 g/10min |
| density | ASTM D792 | 0.978 g/cm³ |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Geon Performance Solutions/Maxxam™ FR PP 301 NATL S |
|---|---|---|---|
| Hot wire ignition | 0.75mm | UL 746 | PLC 4 |
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 0 |
| High arc combustion index | 1.5mm | UL 746 | PLC 1 |
| High voltage arc tracing rate | HVTR | UL 746 | PLC 0 |
| High Voltage Arc Resistance Index (HVAR) | 0.750mm，PLC | UL 746 | PLC 1 |
| Hot wire ignition | 3.0mm | UL 746 | PLC 2 |
| High arc combustion index | 0.75mm | UL 746 | PLC 1 |
| Hot wire ignition | 1.5mm | UL 746 | PLC 3 |
| High Voltage Arc Resistance Index (HVAR) | 3.00mm，PLC | UL 746 | PLC 1 |
| Dielectric strength | ASTM D149 | 41 kV/mm | |
| High Voltage Arc Resistance Index (HVAR) | 1.50mm，PLC | UL 746 | PLC 1 |
| High arc combustion index | 3.0mm | UL 746 | PLC 1 |