mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE KOREA/DF004PSI-GY7G546
Tensile modulus	--2	ASTM D638	5510 Mpa
tensile strength	Break	ASTM D638	91.0 Mpa
Tensile modulus	--	ISO 527-2/1	6000 Mpa
bending strength	Break, 50.0 mm Span	ASTM D790	148 Mpa
Bending modulus	50.0 mm Span	ASTM D790	5510 Mpa
elongation	Break	ASTM D638	9.5 %

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE KOREA/DF004PSI-GY7G546
drying time			4.0 hr
Screw speed			30 to 60 rpm
Suggested maximum moisture content			0.020 %
Temperature in the middle of the barrel			310 to 320 °C
Mold temperature			80 to 110 °C
Temperature at the rear of the barrel			295 to 305 °C
Processing (melt) temperature			305 to 325 °C
drying temperature			120 °C
Temperature at the front of the material cylinder			320 to 330 °C
Back pressure			0.200 to 0.300 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE KOREA/DF004PSI-GY7G546
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	144 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span5	ISO 75-2/Af	142 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE KOREA/DF004PSI-GY7G546
Water absorption rate	24 hr, 50% RH	ASTM D570	0.10 %
Shrinkage rate	Flow : 24hr	ASTM D955	0.20 %
		Flow : 24hr	ISO 294-4	0.20 %
		Across FlowFlow : 24hr	ASTM D955	0.50 %
		横向Flow : 24hr	ISO 294-4	0.45 %