mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TAIWAN POLYPLASTICS/S475 BK210P
Tensile strain	Break	ISO 527-2/1A/5	1.8 %
bending strength	23°C	ISO 178	180 Mpa
Fracture bending strain		ISO 178	2.4 %
tensile strength	Break	ISO 527-2/1A/5	135 Mpa
Bending modulus	23°C	ISO 178	12000 Mpa
Tensile modulus		ISO 527-2/1A	12300 Mpa

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	TAIWAN POLYPLASTICS/S475 BK210P
drying time			6.0 hr
Injection speed			中等
Suggested maximum moisture content			0.010 %
Temperature in the middle of the barrel			340 to 360 °C
Mold temperature			80 to 120 °C
Temperature at the rear of the barrel			330 to 350 °C
Processing (melt) temperature			360 to 375 °C
Hopper temperature			20 to 40 °C
drying temperature			150 °C
Temperature at the front of the material cylinder			345 to 365 °C
Back pressure			< 3.00 Mpa
Spray nozzle temperature			355 to 370 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TAIWAN POLYPLASTICS/S475 BK210P
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	213 °C
Melting temperature		ISO 11357-3	350 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	305 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow	ISO 11359-2	1.0E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TAIWAN POLYPLASTICS/S475 BK210P
Shrinkage rate	横向Flow	ISO 294-4	0.40 %
Shrinkage rate		Flow	ISO 294-4	0.0 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TAIWAN POLYPLASTICS/S475 BK210P
Relative permittivity	1 MHz	IEC 60250	3.70
Dissipation factor	1 MHz	IEC 60250	8.0E-3