mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Eastman Chemical Company/Neostar™ FN006
tensile strength	Yield,23°C,3.00mm,Injection3	ASTM D638	14.0 MPa
Tensile modulus	23°C	ASTM D638	170 MPa
elongation	Yield,23°C	ASTM D638	38 %
Bending modulus	23°C	ASTM D790	150 MPa
elongation	Break,23°C	ASTM D638	400 %
tensile strength	Break,23°C,2.00mm4	ASTM D638	22.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Eastman Chemical Company/Neostar™ FN006
Melting temperature		ASTM D3418	205 °C
thermal conductivity	23°C	ASTMC177	0.19 W/m/K
Glass transition temperature		DSC	-3.00 °C
specific heat	175°C6	DSC	2300 J/kg/°C
specific heat		150°C6	DSC	2000 J/kg/°C
Vicat softening temperature		ASTM D15255	170 °C
specific heat	25°C6	DSC	1600 J/kg/°C
		200°C7	DSC	3100 J/kg/°C
		225°C8	DSC	2300 J/kg/°C
		100°C6	DSC	1800 J/kg/°C
Fusion temperature	23°C	ASTME793	27.0 kJ/kg
Linear coefficient of thermal expansion	MD：23°C	ASTM D696	1.5E-04 cm/cm/°C
Crystallization peak temperature	DSC	DSC	140 °C
Brittle temperature		ASTM D746	<-75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Eastman Chemical Company/Neostar™ FN006
Intrinsic viscosity	23°C	Internal Method	1.2
melt mass-flow rate	230°C/2.16kg	ASTM D1238	10 g/10min
Water absorption rate	23°C,24hr	ASTM D570	0.40 %
density		ASTM D792	1.13 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Eastman Chemical Company/Neostar™ FN006
Shore hardness	ShoreD,23°C	ASTM D2240	55
Shore hardness		ShoreA,23°C	ASTM D2240	95

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Eastman Chemical Company/Neostar™ FN006
tear strength	23°C	ASTM D1004	350 N