So sánh vật liệu
Thông số kỹ thuật
| optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| turbidity | 2540μm | ASTM D1003 | 1.0 % |
| Refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540μm | ASTM D1003 | 88.0 % |
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 3200 J/m |
| ASTM D1822 | 546 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| Bending modulus | 50.0mmSpan | ASTM D790 | 2340 MPa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 93.1 MPa |
| tensile strength | Break | ASTM D638 | 65.5 MPa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTM D1044 | 10.0 mg |
| elongation | Yield | ASTM D638 | 7.0 % |
| tensile strength | Yield | ASTM D638 | 62.1 MPa |
| elongation | Break | ASTM D638 | 110 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| specific heat | ASTMC351 | 1260 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTM D648 | 132 °C |
| 0.45MPa,Unannealed,6.40mm | ASTM D648 | 138 °C | |
| Vicat softening temperature | ASTM D15255 | 154 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| Water absorption rate | Equilibrium,100°C | ASTM D570 | 0.58 % |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50to0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 11 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| Equilibrium,23°C | ASTM D570 | 0.35 % | |
| density | ASTM D792 | 1.20 g/cm³ |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Chase Plastics Services Inc./Polycarbonate PC100RULUV-10M BT Clear |
|---|---|---|---|
| Rockwell hardness | M-Sale | ASTM D785 | 70 |
| R-Sale | ASTM D785 | 118 |