mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	LG GUANGZHOU/GP2102
bending strength	23°C, 3.20 mm, Injection	ASTM D790	98.1 Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	15 %
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	53.9 Mpa
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	3330 Mpa

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	LG GUANGZHOU/GP2102
Minimum Moisture Content			0.020 %
drying time			3.0 to 5.0 hr
Screw speed			40 to 70 rpm
Suggested maximum moisture content			0.020 %
Temperature in the middle of the barrel			285 to 300 °C
Mold temperature			90 to 110 °C
Temperature at the rear of the barrel			280 to 295 °C
Processing (melt) temperature			295 to 310 °C
drying temperature			100 to 120 °C
Temperature at the front of the material cylinder			290 to 305 °C
Back pressure			0.981 to 3.92 Mpa
Spray nozzle temperature			290 to 305 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	LG GUANGZHOU/GP2102
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	80.0 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	137 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	LG GUANGZHOU/GP2102
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	9.0 g/10 min
density		ASTM D792	1.25 g/cm³
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.20 - 0.40 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	LG GUANGZHOU/GP2102
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	124