impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	USA Fulu/HPP40GR27HB BLACK
Dart impact	23°C	ASTM D5420	0.395 J
Impact strength of cantilever beam gap	23°C	ASTM D256	69 J/m
Impact strength of cantilever beam gap		23°C	ASTM D4812	320 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	USA Fulu/HPP40GR27HB BLACK
elongation	Break, 23℃	ASTM D638	3.5 %
Bending modulus	1%Secant:23°C	ASTM D790	6140 MPa
bending strength	23°C	ASTM D790	105 MPa
Bending modulus	1% Secant: 23℃	ASTM D790	6140 MPa
Bending modulus		Tangent:23°C	ASTM D790	6830 MPa
Dart impact	23℃	ASTM D5420	0.395 J
Impact strength of cantilever beam gap	23℃	ASTM D256	69 J/m
tensile strength	23°C	ASTM D638	53.1 MPa
Suspended wall beam without notch impact strength	23℃	ASTM D4812	320 J/m
bending strength	23℃	ASTM D790	105 MPa
tensile strength	23℃	ASTM D638	53.1 MPa
Bending modulus	Tangent: 23℃	ASTM D790	6830 MPa
elongation	Break,23°C	ASTM D638	3.5 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	USA Fulu/HPP40GR27HB BLACK
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	143 °C
		1.8 MPa, Unannealed	ASTM D648	143 ℃
		0.45MPa,Unannealed	ASTM D648	157 °C
		0.45 MPa, Unannealed	ASTM D648	157 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	USA Fulu/HPP40GR27HB BLACK
density		ASTM D792	1.24 g/cm3
melt mass-flow rate	230°C/2.16kg	ASTM D1238	5.5 g/10min
Shrinkage rate	MD	ASTM D955	0.40 %
melt mass-flow rate	230℃/2.16 kg	ASTM D1238	5.5 g/10min
Shrinkage rate	TD	ASTM D955	0.8 %
density		ASTM D792	1.24 g/cm³