mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE SINGAPHORE/C1200HF-111
tensile strength	Yield	ASTM D638	57.0 Mpa
Tensile modulus		ASTM D638	2270 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	88.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2340 Mpa
elongation	Yield	ASTM D638	5.0 %
elongation		Break	ASTM D638	100 %

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE SINGAPHORE/C1200HF-111
Suggested maximum moisture content			0.020 %
Mold temperature			60 to 90 °C
Processing (melt) temperature			275 to 300 °C
drying temperature			100 to 110 °C
Suggested injection volume			30 to 80 %
drying time			3.0 to 4.0 hr
Screw speed			40 to 70 rpm
Temperature in the middle of the barrel			255 to 295 °C
Temperature at the rear of the barrel			250 to 290 °C
Exhaust hole depth			0.038 to 0.076 mm
Hopper temperature			60 to 80 °C
Temperature at the front of the material cylinder			260 to 300 °C
Back pressure			0.300 to 0.700 Mpa
Spray nozzle temperature			275 to 300 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE SINGAPHORE/C1200HF-111
RTI Elec		UL 746	105 °C
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	129 °C
Hot deformation temperature		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	112 °C
RTI Imp		UL 746	80.0 °C
Vicat softening temperature		ISO 306/B50	130 °C
RTI		UL 746	105 °C
Linear coefficient of thermal expansion	-40 to 40°C，Flow	ASTM E831	7.2E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE SINGAPHORE/C1200HF-111
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	19 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

Electrical performance	Phương pháp kiểm tra	SABIC INNOVATIVE SINGAPHORE/C1200HF-111
Hot wire ignition	UL 746	PLC 3
Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	UL 746	PLC 1