	Điều kiện kiểm tra	Phương pháp kiểm tra	INEOS Barex/NAS® 30
turbidity		ASTM D1003	0.30 %
Impact strength of cantilever beam gap	23°C	ASTM D256	21 J/m
bending strength		ISO 178	100 MPa
Refractive index		ASTM D542	1.560
Impact strength of simply supported beam without notch	23°C	ISO 179	12 kJ/m²
Vicat softening temperature		ISO 306/B50	98.0 °C
Ball Pressure Test		ISO 2039-1	169 MPa
Rockwell hardness	M-Scale	ASTM D785	75
Impact strength of cantilever beam gap	23°C	ISO 180/A	2.5 kJ/m²
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	30.0 cm³/10min
Charpy Notched Impact Strength	23°C	ISO 179	1.5 kJ/m²
Shrinkage rate		ISO 294-4	0.20to0.60 %
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	80.0 °C
tensile strength	Yield,23°C	ISO 527-2	60.0 MPa
Refractive index		ISO 489	1.560
Tensile modulus		ASTM D638	3240 MPa
Shrinkage rate	MD	ASTM D955	0.20to0.60 %
Maximum operating temperature			260 °C
density		ISO 1183	1.09 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	2.2 g/10min
bending strength		ASTM D790	101 MPa
density		ASTM D792	1.09 g/cm³
Vicat softening temperature		ASTM D15253	104 °C
elongation	Break	ASTM D638	2.3 %
Suspended wall beam without notch impact strength		ISO 180	12 kJ/m²
Bending modulus		ISO 178	3400 MPa
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	90.0 °C
Water absorption rate	Saturation,23°C	ASTM D570	0.15 %
Tensile strain	Break,23°C	ISO 527-2	2.5 %
tensile strength	Yield,23°C	ASTM D638	60.7 MPa
Bending modulus		ASTM D790	3170 MPa
transmissivity	550nm	ASTM D1003	91.4 %
Tensile modulus		ISO 527-2	3300 MPa