So sánh vật liệu
Thông số kỹ thuật
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | V-0 |
| 0.75 mm | UL 94 | V-2 | |
| 1.5 mm | UL 94 | V-0 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| tensile strength | Break2 | ASTM D638 | 59.0 Mpa |
| Tensile modulus | --2 | ASTM D638 | 2000 Mpa |
| bending strength | --4 | ISO 178 | 80.0 Mpa |
| elongation | Break2 | ASTM D638 | 100 % |
| Bending modulus | --3 | ASTM D790 | 2100 Mpa |
| bending strength | --3 | ASTM D790 | 78.0 Mpa |
| tensile strength | Yield | ISO 527-2/50 | 55.0 Mpa |
| Bending modulus | --4 | ISO 178 | 2100 Mpa |
| tensile strength | Break | ISO 527-2/50 | 60.0 Mpa |
| Tensile modulus | -- | ISO 527-2/50 | 2000 Mpa |
| tensile strength | Yield2 | ASTM D638 | 58.0 Mpa |
| elongation | Break | ISO 527-2/50 | 100 % |
| injection | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| Injection pressure | 68.6 to 127 Mpa | ||
| Suggested maximum moisture content | 0.020 % | ||
| Mold temperature | 70 to 100 °C | ||
| Hot air dryer | 4.0 hr | ||
| Vacuum drying machine | 4.0 hr | ||
| 100 to 120 °C | |||
| Screw speed | 60 to 90 rpm | ||
| Temperature in the middle of the barrel | 240 to 280 °C | ||
| Temperature at the rear of the barrel | 220 to 260 °C | ||
| Temperature at the front of the material cylinder | 260 to 300 °C | ||
| Back pressure | 0.981 to 1.96 Mpa | ||
| Hot air dryer | 100 to 120 °C | ||
| Spray nozzle temperature | 260 to 300 °C |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 123 °C |
| Vicat softening temperature | ISO 306/B50 | 142 °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 126 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| Shrinkage rate | 横向Flow : 2.00 mm | ISO 294-4 | 0.40 - 0.70 % |
| Across FlowFlow : 3.20 mm | ASTM D955 | 0.40 - 0.70 % | |
| melt mass-flow rate | 250°C/10.0 kg | ASTM D1238 | 30 g/10 min |
| Shrinkage rate | Flow : 3.20 mm | ASTM D955 | 0.40 - 0.70 % |
| Flow : 2.00 mm | ISO 294-4 | 0.40 - 0.70 % |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | LOTTE CHEM DONGGUAN/EN-1052W FWA096 |
|---|---|---|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 119 |
| R-Scale | ASTM D785 | 118 |