So sánh vật liệu
Thông số kỹ thuật
| optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE CANADA/HP2R-112 |
|---|---|---|---|
| turbidity | 2540μm | ASTM D1003 | <0.80 % |
| transmissivity | 2540μm | ASTM D1003 | 88.0 % |
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE CANADA/HP2R-112 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eA | 10 kJ/m² | |
| ASTM D256 | 30 J/m | ||
| 23°C | ISO 179/2C | 35 kJ/m² | |
| ASTM D256 | 70 J/m | ||
| ISO 179/1eA | 65 kJ/m² | ||
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 633 J |
| -30°C | ISO 180/1A | 10 kJ/m² | |
| 23°C | ISO 180/1A | 60 kJ/m² |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE CANADA/HP2R-112 |
|---|---|---|---|
| yield | ASTM D638 | 7.0 % | |
| crack | ISO 527-2/50 | 100 % | |
| ASTM D638 | 700 Mpa | ||
| --2 | ASTM D638 | 630 Mpa | |
| yield | ASTM D638 | 630 Mpa | |
| 50.0mm span | ASTM D790 | 2350 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 980 Mpa | |
| --9 | ISO 178 | 90.0 Mpa | |
| crack | ASTM D638 | 130 % | |
| yield | ISO 527-2/50 | 6.0 % | |
| --8 | ISO 178 | 2300 Mpa | |
| crack | ISO 527-2/50 | 65.0 Mpa | |
| yield | ISO 527-2/50 | 63.0 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE CANADA/HP2R-112 |
|---|---|---|---|
| Horizontal: -40 to 40 ° C | Across Flow, -40to40℃ | ASTME831 | 6.8E-05 cm/cm/°C |
| 1.8MPa, unannealed, 100mm span | ISO 75-2/Ae | 122 °C | |
| Flow: 23 to 80 ° C | 23to80℃ | ISO 11359-2 | 7E-05 cm/cm/°C |
| Horizontal: -40 to 40 ° C | Across Flow, -40to40℃ | ISO 11359-2 | 7E-05 cm/cm/°C |
| 0.45MPa, unannealed, 100mm span | ISO 75-2/Be | 133 °C | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 129 °C | |
| Flow: -40 to 40 ° C | ASTME831 | 6.8E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE CANADA/HP2R-112 |
|---|---|---|---|
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.50-0.70 % |
| MD：--1 | Internal Method | 0.50-0.70 % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.35 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 22 g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 21.0 cm3/10min |