So sánh vật liệu
Thông số kỹ thuật
impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 160 J/m |
Instrumented dart impact energy -30 ℃ (-22 ℉) peak | ASTM D3763 | 54 J | |
Instrumented dart impact energy 23 ℃ (73 ℉) total energy | ASTM D3763 | 61 J | |
Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 534 J/m |
mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
bending strength | 2.6 mm/,Yield | ASTM D790 | 102 Mpa |
Bending modulus | 2.6 mm/ | ASTM D790 | 2650 Mpa |
tensile strength | Type I, 50,Yield | ASTM D638 | 62 Mpa |
Elongation at Break | Type I, 50 | ASTM D638 | 40 |
thermal properties | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Vicat softening temperature | Rate B/50 | ASTM D1525 | 85 °C |
thermal conductivity | ASTM C 177 | 0.2 W/m-°C | |
Linear coefficient of thermal expansion | -30°C to 3,Across Flow | ASTM E831 | 72 E-6/°C |
RTI Imp | UL 746B | 85 °C | |
RTI Elec | UL 746B | 85 °C | |
Linear coefficient of thermal expansion | -30°C to 3,Flow | ASTM E831 | 72 E-6/°C |
combustion performance | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Limiting Oxygen Index (LOI) | ASTM D 2863 | 32 % | |
UL fire rating V | UL 94 | 1.5 mm | |
UL fire rating 5VB | UL 94 | 2.49 mm |
Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Water absorption rate | 24 hours | ASTM D570 | 0.1 |
Shrinkage rate | xflow, 3.2 | Internal | 0.4-0.6 |
Water absorption rate | flow, 3.2 | ASTM D570 | 0.4 |
melt mass-flow rate | ASTM D1238 | 10 g/10min | |
Shrinkage rate | flow, 3.2 | Internal | 0.4-0.8 |
Electrical Property | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Surface resistivity | ASTM D257 | 10000000000000000 Ohm | |
Compared to the Leakage Traceability Index (CTI) | UL 746A | PLC_0 | |
High voltage arc tracing rate | UL 746A | PLC 2 | |
Volume resistivity | ASTM D257 | 100000000000000000 ohm-cm | |
Dissipation factor | ASTM D 150 | 49 E-4 | |
High current arc ignition (HAI) | UL 746A | PLC_0 | |
Arc resistance | ASTM D495 | PLC_6 | |
Dielectric strength | in oil, 3.2 | ASTM D149 | 19.5 kV/mm |
Hot wire ignition (HWI) | UL 746A | PLC_1 | |
Dielectric constant | ASTM D 150 | 3 |
hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | SABIC INNOVATIVE US/C2950-701NSDD |
---|---|---|---|
Hardness (Rockwell R) | ASTM D785 | 123 R |