	Điều kiện kiểm tra	Phương pháp kiểm tra	Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® SuperPlus
UL flame retardant rating	3.2mm	UL 94	HB
Linear coefficient of thermal expansion	MD2：-40to149°C	ASTME831	2.2E-04 cm/cm/°C
Shore hardness	ShoreD	ASTM D2240	70
density		ASTM D792	0.960 g/cm³
Dielectric constant	1MHz	ASTM D150	2.30
elongation	Break	ASTM D638	300 %
Crystallization peak temperature	DSC	ASTM D3418	135 °C
Maximum operating temperature LongTerm, Air			104 °C
Water absorption rate	Saturation	ASTM D570	<0.010 %
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	46.7 °C
limiting pv value		Internal Method	0.0701 MPa·m/s
compressive strength	10%Strain,23°C	ASTM D695	20.7 MPa
Compressive modulus		ASTM D695	414 MPa
Water absorption rate	24hr	ASTM D570	<0.010 %
Surface resistivity		ASTM D257	>1.0E+15 ohms
tensile strength	Ultimate	ASTM D638	36.5 MPa
Dissipation factor	1MHz	ASTM D150	5E-04
Bending modulus		ASTM D790	586 MPa
Friction coefficient	Steel - Static	Internal Method	0.15
thermal conductivity			0.41 W/m/K
Tensile modulus		ASTM D638	703 MPa
bending strength	Yield	ASTM D790	21.4 MPa
Impact strength of cantilever beam gap		ASTM D256A	无断裂
Dielectric strength		ASTM D149	91 kV/mm