impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	BASF SHANGHAI/B3WG6 BK00564
Impact strength of simply supported beam without notch	-30°C	ISO 179	65 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	9.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	12 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	150 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179	80 kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	110 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	BASF SHANGHAI/B3WG6 BK00564
tensile strength	Break,23°C	ISO 527-2	180 Mpa
Tensile modulus	23°C	ISO 527-2	9500 Mpa
Bending modulus	23°C	ISO 178	8300 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
tensile strength	Break,23°C	ASTM D638	180 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	BASF SHANGHAI/B3WG6 BK00564
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	210 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature			ISO 3146	220 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
		1.8MPa,Unannealed	ISO 75-2/A	205 °C
		0.45MPa,Unannealed	ASTM D648	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	BASF SHANGHAI/B3WG6 BK00564
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0 cm3/10min
Water absorption rate	Saturation	ASTM D570	6.6 %
Water absorption rate		Equilibrium,23°C,50%RH	ISO 62	2.1 %
density		ISO 1183	1.36 g/cm³
Water absorption rate	Equilibrium,50%RH	ASTM D570	2.1 %
Water absorption rate		Saturation,23°C	ISO 62	6.6 %
Shrinkage rate	MD：3.18mm		0.30 %
density		ASTM D792	1.36 g/cm³