injection	Điều kiện kiểm tra	Phương pháp kiểm tra	TOTAL THAILAND/L130
Dew point temperature			< -40 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.025 %
Temperature in the middle of the barrel			180 to 220 °C
Temperature at the rear of the barrel			155 to 175 °C
Processing (melt) temperature			180 to 220 °C
Hopper temperature			20 to 40 °C
drying temperature			100 °C
Back pressure			5.00 to 10.0 Mpa
Temperature at the front of the material cylinder			180 to 220 °C
Spray nozzle temperature			180 to 220 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TOTAL THAILAND/L130
Hot deformation temperature	0.45 MPa, Unannealed3	ISO 75-2/Bf	55.0 to 60.0 °C
Melting temperature		DSC	175 °C
Hot deformation temperature	0.45 MPa, Unannealed4	ISO 75-2/Bf	100 to 110 °C
Monomer Residue		Internal Method	< 0.30 %
Glass transition temperature		DSC	55.0 to 60.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TOTAL THAILAND/L130
melt mass-flow rate	210°C/2.16 kg	ISO 1133	16 g/10 min
water content		Karl Fisher	< 400 ppm
melt mass-flow rate	190°C/2.16 kg	ISO 1133	7.0 g/10 min