mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE CANADA/FR23 BK4051
tensile strength	Yield	ASTM D638	42.0 Mpa
Tensile modulus		ASTM D638	2410 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	73.0 Mpa
tensile strength	Break	ASTM D638	35.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2720 Mpa
elongation	Yield	ASTM D638	2.1 %
elongation		Break	ASTM D638	11 %

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE CANADA/FR23 BK4051
Suggested maximum moisture content			0.10 %
Mold temperature			50 to 70 °C
Processing (melt) temperature			200 to 220 °C
drying temperature			80 to 90 °C
Suggested injection volume			50 to 70 %
drying time			2.0 to 4.0 hr
Screw speed			30 to 60 rpm
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the rear of the barrel			170 to 180 °C
Exhaust hole depth			0.038 to 0.051 mm
Temperature at the front of the material cylinder			200 to 215 °C
Back pressure			0.300 to 0.700 Mpa
Spray nozzle temperature			200 to 220 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE CANADA/FR23 BK4051
RTI Elec		UL 746	60.0 °C
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	83.0 °C
Hot deformation temperature		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	72.0 °C
RTI Imp		UL 746	60.0 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
RTI		UL 746	60.0 °C
Vicat softening temperature		ASTM D15255	90.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE CANADA/FR23 BK4051
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
melt mass-flow rate	230°C/3.8 kg	ASTM D1238	6.8 g/10 min
melt mass-flow rate		220°C/5.0 kg	ISO 1133	9.0 g/10 min
Melt Volume Flow Rate (MVR)	220°C/10.0 kg	ISO 1133	37.0 cm3/10min