So sánh vật liệu
Thông số kỹ thuật
| Điều kiện kiểm tra | Phương pháp kiểm tra | Mitsubishi Chemical Advanced Materials/Quadrant EPP CESTILENE HD 1000 R | |
|---|---|---|---|
| Shore hardness | ShoreD,3Sec | ISO 868 | 63 |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Vicat softening temperature | ISO 306/B | 80.0 °C | |
| Nominal tensile fracture strain | ISO 527-2/1B/50 | >50 % | |
| Ball Pressure Test | ISO 2039-1 | 38.0 MPa | |
| Shore hardness | ShoreD,15Sec | ISO 868 | 61 |
| thermal conductivity | 23°C | 0.40 W/m/K | |
| Tensile strain | Yield | ISO 527-2/1B/50 | 13 % |
| Charpy Notched Impact Strength | --2 | Internal Method | >80 kJ/m² |
| tensile strength | Yield | ISO 527-2/1B/50 | 22.0 MPa |
| Charpy Notched Impact Strength | Partial Break | ISO 179/1eA | >90 kJ/m² |
| Tensile modulus | ISO 527-2/1B/1 | 950 MPa | |
| Linear coefficient of thermal expansion | MD：23to100°C | 2E-04 cm/cm/°C | |
| density | ISO 1183 | 0.930 g/cm³ | |
| Compressive stress | 2%Strain | ISO 604/1 | 10.5 MPa |
| Continuous use temperature | --4 | 120 °C | |
| molecular weight distribution | 4000000 g/mol | ||
| Compressive stress | 5%Strain | ISO 604/1 | 18.0 MPa |
| 1%Strain | ISO 604/1 | 6.00 MPa | |
| Melting temperature | ISO 11357-3 | 130to135 °C | |
| Relative Weight Loss | --6 | Internal Method | 150 |
| --5 | Internal Method | 180 | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Water absorption rate | Saturation,23°C,1.00mm | ISO 62 | 0.020 % |
| Minimum operating temperature | -150 °C | ||
| Continuous use temperature | --3 | 80.0 °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 42.0 °C |
| Extreme Oxygen Index | ISO 4589-2 | <20 % |