TPU-Ether Texin® 950 Covestro - Polycarbonates

--

--

--

- -
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Thông số kỹ thuật

elastomerĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
Permanent compression deformation23°C,22hrASTMD395B20 %
tensile strength100%StrainASTMD41213.8 MPa
elongationBreakASTMD412470 %
Shore hardnessASTM D263235 %
tensile strengthYieldASTMD41249.0 MPa
Permanent compression deformation70°C,22hr3ASTMD395B40 %
tear strength--ISO 34-1130 kN/m
tensile strength300%StrainASTMD41227.6 MPa
50%StrainASTMD41212.1 MPa
tear strength--2ASTM D624131 kN/m
Permanent compression deformation23°C,22hr3ASTMD395B15 %
70°C,22hrASTMD395B70 %
mechanical propertiesĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
Bending modulus23°CASTMD790114 MPa
Taber abraser1000Cycles,1000g,H-18WheelISO 464975.0 mg
1000Cycles,1000g,H-18WheelASTM D104475.0 mg
Bending modulus70°CASTMD79046.9 MPa
thermal performanceĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
Vicat softening temperatureISO 306/50128 °C
Brittle temperatureASTMD746<-68.0 °C
Linear coefficient of thermal expansionMDASTM D6961.3E-04 cm/cm/°C
Glass transition temperatureDMA-27.0 °C
Physical propertiesĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
densityASTMD7921.15 g/cm³
Shrinkage rateTD:2.54mmISO 25770.80 %
MD:2.54mmISO 25770.80 %
TD:2.54mmASTM D9550.80 %
MD:2.54mmASTM D9550.80 %
hardnessĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
Shore hardnessShoreDASTMD224050
agingĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
Change rate of tensile strength in air300%Strain,125°C,336hrASTM D573-22 %
300%Strain125°C,70hrISO 216-7.0 %
Change rate of ultimate elongation in air100°C,168hr,在ASTM#3油中ISO 17525 %
Change rate of tensile strength in air125°C,168hrASTMD573-27 %
100%Strain,125°C,70hrASTM D5731.0 %
Change rate of hardness (Shore) in the air支撐D,125°C,336hrASTMD573-1.0
Volume change23°C,168hr,在基准燃料C中ISO 17526 %
Change rate of hardness (Shore) in the air支撐D,100°C,336hr,在ASTM#1油中ASTMD4710.0
Change rate of tensile strength in air100%Strain,100°C,336hr,在ASTM#1油中ASTMD4718.0 %
Volume change100°C,168hr,ASTM标准油（3号）ASTM D47110 %
100°C,504hr,ASTM标准油（3号）ASTM D47113 %
Change rate of tensile strength in air100%Strain100°C,504hrISO 2165.0 %
100°C,336hr,在ASTM#1油中ASTMD471-2.0 %
300%Strain,100°C,70hr,在ASTM#3油中ASTM D4713.0 %
100%Strain100°C,70hrISO 2164.0 %
100%Strain,23°C,504hr,在基准燃料A中ASTM D471-4.0 %
Change rate of ultimate elongation in air100°C,504hr,在ASTM#3油中ASTM D47138 %
Change rate of tensile strength in air100°C,168hr,在ASTM#3油中ASTM D47112 %
300%Strain,100°C,336hr,在ASTM#3油中ISO 175-9.0 %
Volume change100°C,504hr,在ASTM#3油中ISO 17513 %
Change rate of hardness (Shore) in the air支撐D,125°C,168hrASTMD573-1.0
支撐D,23°C,70hr,在基准燃料A中ASTM D4711.0
支撐D,100°C,70hr,在ASTM#3油中ISO 1755.0
Change rate of tensile strength in air300%Strain,100°C,504hr,在ASTM#3油中ASTM D471-18 %
23°C,168hr,在参考燃料A中（异辛烷）ISO 17516 %
Change rate of hardness (Shore) in the air支撐D,125°C,70hrASTMD5731.0
支撐D,23°C,70hr,inReferenceFuelCASTMD471-11
Change rate of tensile strength in air23°C,70hr,C级标准燃料ASTM D471-17 %
300%Strain,23°C,504hr,在基准燃料A中ASTM D471-4.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,70hr,在ASTM#1油中ASTMD4710.0
支撐D,23°C,504hr,在基准燃料A中（异辛烷）ISO 1752.0
Change rate of tensile strength in air100%Strain,23°C,70hr,在基准燃料A中ASTM D471-3.0 %
Change rate of hardness (Shore) in the air支撐D,125°C,504hrASTMD5731.0
Change rate of tensile strength in air300%Strain100°C,504hrISO 216-3.0 %
300%Strain,125°C,504hrASTM D573-25 %
100%Strain,100°C,504hr,在ASTM#3油中ISO 175-9.0 %
300%Strain,23°C,168hr,在基准燃料A中ASTM D4712.0 %
Change rate of ultimate elongation in air23°C,336hr,在基准燃料A中ASTM D4713.0 %
Change rate of tensile strength in air300%Strain,125°C,168hrASTM D573-18 %
100%Strain,125°C,336hrASTM D5730.0 %
100%Strain,100°C,504hr,在ASTM#3油中ASTM D471-9.0 %
100%Strain,23°C,70hr,C级标准燃料ASTM D471-42 %
100%Strain,23°C,504hr,在参考燃料A中（异辛烷）ISO 175-4.0 %
300%Strain,100°C,504hr,在ASTM#3油中ISO 175-18 %
Change rate of ultimate elongation in air23°C,168hr,在参考燃料A中（异辛烷）ISO 1757.0 %
Change rate of tensile strength in air23°C,336hr,在基准燃料A中ASTM D4717.0 %
Volume change100°C,70hr,ASTM标准油（3号）ASTM D4719.0 %
Change rate of ultimate elongation in air23°C,504hr,C级标准燃料ASTM D471-2.0 %
Change rate of tensile strength in air23°C,70hr,inReferenceFuelCISO 175-17 %
Change rate of hardness (Shore) in the air支撐D,23°C,70hr,在基准燃料A中（异辛烷）ISO 1751.0
Change rate of tensile strength in air100°C,168hr,在ASTM#1油中ASTMD4710.0 %
300%Strain,100°C,168hr,在ASTM#1油中ASTMD4710.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,168hrASTMD5730.0
Change rate of tensile strength in air100%Strain,23°C,504hr,C级标准燃料ASTM D471-36 %
Change rate of ultimate elongation in air125°C,336hrASTMD57312 %
100°C,504hr,在ASTM#1油中ASTMD47132 %
Volume change23°C,504hr,A级标准燃料ASTM D4711.0 %
Change rate of tensile strength in air300%Strain,23°C,168hr,inReferenceFuelCISO 175-30 %
300%Strain,23°C,336hr,inReferenceFuelCISO 175-33 %
100%Strain,100°C,336hrASTM D5734.0 %
100%Strain,100°C,70hrASTM D5734.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,70hr,在ASTM#3油中ASTM D4715.0
Change rate of tensile strength in air100%Strain,100°C,504hr,在ASTM#1油中ASTMD4714.0 %
Change rate of ultimate elongation in air23°C,336hr,C级标准燃料ASTM D471-5.0 %
Change rate of tensile strength in air100%Strain,100°C,168hr,在ASTM#1油中ASTMD4714.0 %
100%Strain,100°C,70hr,在ASTM#1油中ASTMD4717.0 %
300%Strain,23°C,504hr,inReferenceFuelCISO 175-51 %
125°C,504hrASTMD573-44 %
300%Strain,100°C,336hr,在ASTM#1油中ASTMD4710.0 %
100%Strain,23°C,168hr,在基准燃料A中ASTM D4716.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,70hrASTMD573-1.0
Change rate of tensile strength in air100%Strain100°C,336hrISO 2164.0 %
Change rate of ultimate elongation in air23°C,168hr,C级标准燃料ASTM D471-6.0 %
Change rate of tensile strength in air23°C,70hr,在参考燃料A中（异辛烷）ISO 17516 %
300%Strain100°C,70hrISO 2162.0 %
Change rate of ultimate elongation in air100°C,336hr,在ASTM#1油中ASTMD47123 %
Change rate of tensile strength in air300%Strain,100°C,168hrASTM D573-1.0 %
Volume change100°C,70hr,在ASTM#1油中ISO 1750.0 %
23°C,168hr,A级标准燃料ASTM D4711.0 %
Change rate of tensile strength in air100°C,504hr,在ASTM#3油中ASTM D4711.0 %
100°C,168hr,在ASTM#3油中ISO 17512 %
Change rate of hardness (Shore) in the air支撐D,23°C,168hr,在基准燃料A中ASTM D4711.0
支撐D,23°C,168hr,inReferenceFuelCASTMD471-13
支撐D,23°C,504hr,inReferenceFuelCASTMD471-13
支撐D,23°C,336hr,inReferenceFuelCASTMD471-10
Change rate of tensile strength in air23°C,168hr,inReferenceFuelCISO 175-17 %
100%Strain,100°C,168hrASTM D5734.0 %
23°C,504hr,inReferenceFuelCISO 175-15 %
Change rate of hardness (Shore) in the air支撐D,23°C,336hr,在基准燃料A中（异辛烷）ISO 1750.0
Change rate of tensile strength in air23°C,168hr,C级标准燃料ASTM D471-17 %
100%Strain,100°C,168hr,在ASTM#3油中ISO 175-7.0 %
125°C,70hrASTMD573-11 %
300%Strain,23°C,504hr,C级标准燃料ASTM D471-51 %
100°C,70hrASTMD5732.0 %
Volume change23°C,168hr,在基准燃料A中ISO 1751.0 %
Change rate of tensile strength in air100°C,336hrASTMD5734.0 %
Volume change23°C,336hr,A级标准燃料ASTM D4711.0 %
Change rate of ultimate elongation in air125°C,168hrASTMD57329 %
100°C,168hr,在ASTM#1油中ASTMD47119 %
Change rate of tensile strength in air100%Strain,100°C,70hr,在ASTM#3油中ISO 1752.0 %
23°C,168hr,在基准燃料A中ASTM D47116 %
Change rate of ultimate elongation in air125°C,70hrASTMD57322 %
Change rate of tensile strength in air100%Strain,23°C,168hr,inReferenceFuelCISO 175-36 %
300%Strain,100°C,70hr,在ASTM#1油中ASTMD4714.0 %
Change rate of ultimate elongation in air23°C,168hr,在基准燃料A中ASTM D4717.0 %
Change rate of tensile strength in air300%Strain100°C,336hrISO 216-2.0 %
100%Strain,125°C,504hrASTM D573-5.0 %
Volume change100°C,336hr,ASTM标准油（1号）ASTM D4710.0 %
Change rate of tensile strength in air300%Strain,100°C,504hr,在ASTM#1油中ASTMD471-7.0 %
300%Strain,100°C,168hr,在ASTM#3油中ISO 175-11 %
300%Strain,23°C,168hr,在参考燃料A中（异辛烷）ISO 1752.0 %
300%Strain,23°C,70hr,在基准燃料A中ASTM D4710.0 %
23°C,336hr,在参考燃料A中（异辛烷）ISO 1757.0 %
100°C,70hr,在ASTM#3油中ASTM D47110 %
100%Strain,23°C,336hr,在参考燃料A中（异辛烷）ISO 1751.0 %
100%Strain,23°C,504hr,inReferenceFuelCISO 175-36 %
100%Strain,23°C,336hr,inReferenceFuelCISO 175-36 %
100°C,336hr,在ASTM#3油中ASTM D471-3.0 %
23°C,336hr,inReferenceFuelCISO 175-20 %
Change rate of ultimate elongation in air100°C,70hr,在ASTM#3油中ASTM D47117 %
Change rate of tensile strength in air300%Strain,23°C,336hr,在基准燃料A中ASTM D4713.0 %
Change rate of ultimate elongation in air23°C,70hr,inReferenceFuelCISO 1750.0 %
100°C,504hr,在ASTM#3油中ISO 17538 %
Volume change100°C,70hr,在ASTM#3油中ISO 1759.0 %
Change rate of tensile strength in air300%Strain,100°C,504hrASTM D573-3.0 %
Volume change23°C,336hr,在基准燃料A中ISO 1751.0 %
Change rate of tensile strength in air300%Strain125°C,504hrISO 216-25 %
Volume change23°C,70hr,C级标准燃料ASTM D47122 %
Change rate of tensile strength in air300%Strain,23°C,70hr,inReferenceFuelCISO 175-36 %
Change rate of hardness (Shore) in the air支撐D,100°C,336hr,在ASTM#3油中ASTM D471-4.0
Change rate of tensile strength in air100%Strain125°C,336hrISO 2160.0 %
300%Strain,23°C,70hr,C级标准燃料ASTM D471-36 %
100°C,70hr,在ASTM#3油中ISO 17510 %
Volume change100°C,168hr,在ASTM#3油中ISO 17510 %
Change rate of hardness (Shore) in the air支撐D,100°C,336hr,在ASTM#3油中ISO 175-4.0
Change rate of ultimate elongation in air23°C,504hr,在基准燃料A中ASTM D4718.0 %
Change rate of tensile strength in air100%Strain,100°C,336hr,在ASTM#3油中ASTM D471-2.0 %
Change rate of ultimate elongation in air100°C,504hrASTMD57316 %
100°C,168hr,在ASTM#3油中ASTM D47125 %
23°C,70hr,C级标准燃料ASTM D4710.0 %
Change rate of tensile strength in air300%Strain,100°C,70hr,在ASTM#3油中ISO 1753.0 %
Volume change23°C,70hr,在基准燃料A中ISO 1750.0 %
23°C,70hr,A级标准燃料ASTM D4710.0 %
23°C,336hr,C级标准燃料ASTM D47126 %
Change rate of tensile strength in air100%Strain,23°C,70hr,inReferenceFuelCISO 175-42 %
Change rate of hardness (Shore) in the air支撐D,23°C,168hr,在基准燃料A中（异辛烷）ISO 1751.0
Change rate of tensile strength in air300%Strain,100°C,336hrASTM D573-2.0 %
Change rate of ultimate elongation in air23°C,504hr,在参考燃料A中（异辛烷）ISO 1758.0 %
Volume change23°C,336hr,在基准燃料C中ISO 17526 %
Change rate of tensile strength in air100%Strain125°C,168hrISO 2164.0 %
Change rate of ultimate elongation in air100°C,336hrASTMD57319 %
100°C,70hrASTMD57310 %
Change rate of tensile strength in air100%Strain,100°C,336hr,在ASTM#3油中ISO 175-2.0 %
100%Strain125°C,504hrISO 216-5.0 %
Volume change100°C,336hr,ASTM标准油（3号）ASTM D47112 %
23°C,168hr,C级标准燃料ASTM D47126 %
Change rate of tensile strength in air100°C,504hrASTMD5733.0 %
300%Strain,100°C,70hrASTM D5732.0 %
300%Strain100°C,168hrISO 216-1.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,504hr,在ASTM#3油中ISO 175-2.0
Change rate of tensile strength in air23°C,336hr,C级标准燃料ASTM D471-20 %
Volume change100°C,336hr,在ASTM#3油中ISO 17512 %
Change rate of tensile strength in air23°C,504hr,在参考燃料A中（异辛烷）ISO 17513 %
100°C,168hrASTMD5732.0 %
100%Strain,23°C,168hr,在参考燃料A中（异辛烷）ISO 1756.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,504hrASTMD573-1.0
Change rate of tensile strength in air100°C,336hr,在ASTM#3油中ISO 175-3.0 %
100%Strain,100°C,70hr,在ASTM#3油中ASTM D4712.0 %
300%Strain,23°C,336hr,C级标准燃料ASTM D471-33 %
300%Strain,23°C,336hr,在参考燃料A中（异辛烷）ISO 1753.0 %
Change rate of hardness (Shore) in the air支撐D,23°C,336hr,在基准燃料A中ASTM D4710.0
Change rate of tensile strength in air23°C,504hr,C级标准燃料ASTM D471-15 %
300%Strain125°C,168hrISO 216-18 %
23°C,70hr,在基准燃料A中ASTM D47116 %
Change rate of ultimate elongation in air100°C,336hr,在ASTM#3油中ISO 17527 %
Volume change23°C,504hr,在基准燃料C中ISO 17526 %
Change rate of hardness (Shore) in the air支撐D,100°C,168hr,在ASTM#1油中ASTMD4712.0
支撐D,100°C,504hr,在ASTM#3油中ASTM D471-2.0
Change rate of tensile strength in air100%Strain,125°C,168hrASTM D5734.0 %
100%Strain125°C,70hrISO 2161.0 %
100°C,70hr,在ASTM#1油中ASTMD4712.0 %
Change rate of ultimate elongation in air100°C,168hrASTMD57315 %
23°C,70hr,在基准燃料A中ASTM D4715.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,168hr,在ASTM#3油中ISO 1755.0
Change rate of tensile strength in air23°C,504hr,在基准燃料A中ASTM D47113 %
Change rate of hardness (Shore) in the air支撐D,100°C,168hr,在ASTM#3油中ASTM D4715.0
Change rate of tensile strength in air100%Strain,23°C,336hr,在基准燃料A中ASTM D4711.0 %
Change rate of ultimate elongation in air23°C,168hr,inReferenceFuelCISO 175-6.0 %
Volume change100°C,168hr,ASTM标准油（1号）ASTM D4710.0 %
Change rate of ultimate elongation in air23°C,336hr,inReferenceFuelCISO 175-5.0 %
Volume change100°C,168hr,在ASTM#1油中ISO 1750.0 %
100°C,504hr,ASTM标准油（1号）ASTM D4710.0 %
Change rate of tensile strength in air300%Strain,23°C,70hr,在参考燃料A中（异辛烷）ISO 1750.0 %
Change rate of ultimate elongation in air100°C,70hr,在ASTM#1油中ASTMD47118 %
Change rate of tensile strength in air100%Strain100°C,168hrISO 2164.0 %
100%Strain,23°C,168hr,C级标准燃料ASTM D471-36 %
Volume change100°C,504hr,在ASTM#1油中ISO 1750.0 %
Change rate of ultimate elongation in air23°C,504hr,inReferenceFuelCISO 175-2.0 %
23°C,70hr,在参考燃料A中（异辛烷）ISO 1755.0 %
Change rate of tensile strength in air100°C,504hr,在ASTM#3油中ISO 1751.0 %
100%Strain,23°C,70hr,在参考燃料A中（异辛烷）ISO 175-3.0 %
300%Strain125°C,336hrISO 216-22 %
300%Strain,125°C,70hrASTM D573-7.0 %
300%Strain,100°C,336hr,在ASTM#3油中ASTM D471-9.0 %
Change rate of hardness (Shore) in the air支撐D,23°C,504hr,在基准燃料A中ASTM D4712.0
Change rate of ultimate elongation in air100°C,70hr,在ASTM#3油中ISO 17517 %
Change rate of tensile strength in air100%Strain,100°C,504hrASTM D5735.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,504hr,在ASTM#1油中ASTMD4712.0
Volume change23°C,504hr,C级标准燃料ASTM D47126 %
Change rate of tensile strength in air125°C,336hrASTMD573-40 %
300%Strain,23°C,168hr,C级标准燃料ASTM D471-30 %
100%Strain,23°C,336hr,C级标准燃料ASTM D471-36 %
300%Strain,23°C,504hr,在参考燃料A中（异辛烷）ISO 175-4.0 %
300%Strain,100°C,168hr,在ASTM#3油中ASTM D471-11 %
Change rate of ultimate elongation in air23°C,336hr,在参考燃料A中（异辛烷）ISO 1753.0 %
Volume change100°C,70hr,ASTM标准油（1号）ASTM D4710.0 %
Change rate of tensile strength in air100°C,504hr,在ASTM#1油中ASTMD471-3.0 %
Volume change23°C,504hr,在基准燃料A中ISO 1751.0 %
23°C,70hr,在基准燃料C中ISO 17522 %
Change rate of tensile strength in air100%Strain,100°C,168hr,在ASTM#3油中ASTM D471-7.0 %
Change rate of hardness (Shore) in the air支撐D,100°C,336hrASTMD573-2.0
Volume change100°C,336hr,在ASTM#1油中ISO 1750.0 %
Change rate of ultimate elongation in air100°C,336hr,在ASTM#3油中ASTM D47127 %
125°C,504hrASTMD5739.0 %
Supplementary InformationĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 950
CompressiveLoad15%DeflectionASTM D5757.58 MPa
25%DeflectionASTM D57512.4 MPa
10%DeflectionASTM D5755.52 MPa
5%DeflectionASTM D5752.93 MPa
50%DeflectionASTM D57531.0 MPa
20%DeflectionASTM D57510.3 MPa
2%DeflectionASTM D5751.03 MPa