So sánh vật liệu
Thông số kỹ thuật
optical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
gloss | 45°,20.3μm | ASTM D2457 | 92 |
45°,50.8μm | ASTM D2457 | 90 | |
transparency | 50.8μm | ASTM D1746 | 99.0 |
gloss | 45° | ASTM D-2457 | 90 |
turbidity | ASTM D-1003 | 1.8 % | |
transparency | ASTM D-1746 | 99 | |
20.3μm | ASTM D1746 | 99.0 | |
turbidity | 20.3μm | ASTM D1003 | 0.60 % |
50.8μm | ASTM D1003 | 1.8 % |
Basic Performance | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
density | ASTM D792 | 0.904 g/cm³ | |
melt mass-flow rate | ASTM D1238 | 4 g/10min |
mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
tensile strength | MD,Break | ASTM D-882 | 33 Mpa |
TD,Break | ASTM D-882 | 32 Mpa | |
Elongation at Break | MD | ASTM D-882 | 664 % |
tensile strength | Yield,TD | ASTM D-882 | 5 Mpa |
Puncture intensity | 陶氏企业测试 | 17 J/cm³ | |
Tensile modulus | MD,3% Secant | ASTM D-882 | 63 Mpa |
tensile strength | Yield,MD | ASTM D-882 | 7 Mpa |
Elongation at Break | TD | ASTM D-882 | 714 % |
Tensile modulus | TD,2% Secant | ASTM D-882 | 63 Mpa |
thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
Vicat softening temperature | ASTM D-1525 | 71 °C | |
Melting temperature | Internal Method | 124 °C | |
Vicat softening temperature | ASTM D1525 | 71.1 °C |
Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 4.0 g/10min |
film | Điều kiện kiểm tra | Phương pháp kiểm tra | STYRON US/4404G |
---|---|---|---|
Elmendorf tear strength | MD:20μm | ASTM D1922 | 330 g |
TD:20μm | ASTM D1922 | 500 g | |
Carbon dioxide transmittance | 23°C,50.8μm | Internal Method | 2000 cm³·mm/m²/atm/24hr |
Dart impact | 20μm | ASTM D1709B | >850 g |
tensile strength | TD:Break,20μm | ASTM D882 | 29.1 Mpa |
elongation | MD:Break,51μm | ASTM D882 | 660 % |
Water vapor permeability | 51μm | ASTMF1249 | 0.85 g·mm/m²/atm/24hr |
tensile strength | MD:Break,20μm | ASTM D882 | 36.9 Mpa |
Secant modulus | 2%Secant,TD:51μm | ASTM D882 | 63.0 Mpa |
elongation | TD:Break,51μm | ASTM D882 | 710 % |
tensile strength | MD:Yield,20μm | ASTM D882 | 7.00 Mpa |
TD:Yield,51μm | ASTM D882 | 6.34 Mpa | |
Thin film puncture strength | 51μm | Internal Method | 17.5 J/cm³ |
Secant modulus | 2%Secant,MD:20μm | ASTM D882 | 58.8 Mpa |
Elmendorf tear strength | MD:51μm | ASTM D1922 | 960 g |
TD:51μm | ASTM D1922 | 1100 g | |
tensile strength | TD:Break,51μm | ASTM D882 | 32.4 Mpa |
Dart impact | 51μm | ASTM D1709B | >850 g |
elongation | MD:Break,20μm | ASTM D882 | 500 % |
tensile strength | MD:Break,51μm | ASTM D882 | 32.6 Mpa |
Secant modulus | 2%Secant,TD:20μm | ASTM D882 | 64.7 Mpa |
Thin film puncture strength | 20μm | Internal Method | 18.9 J/cm³ |
tensile strength | MD:Yield,51μm | ASTM D882 | 6.76 Mpa |
elongation | TD:Break,20μm | ASTM D882 | 710 % |
tensile strength | TD:Yield,20μm | ASTM D882 | 4.92 Mpa |
Oxygen permeability | 23°C,51μm | ASTM D3985 | 450 cm³·mm/m²/atm/24hr |
Secant modulus | 2%Secant,MD:51μm | ASTM D882 | 62.6 Mpa |