mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
Friction coefficient			0.30
tensile strength		ASTM D638/ISO 527	115 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	123
shear strength	23°C	JISK7214	60.0 Mpa
tensile strength		ASTM D-638	1.2 %
Elongation at Break		ASTM D-732	60
Tensile strain	Break,23°C	ISO 527-2	0.80 %
Elongation at Break		ASTM D638/ISO 527	0.8 %
Impact strength of cantilever beam gap	Notched23℃	ASTM D-256	90 J/m
bending strength		ASTM D790/ISO 178	200 kg/cm²(MPa)[Lb/in²]
bending strength		23°C	ISO 178	200 Mpa
abrasion		ASTM D-1044	70 mg/1000回
tensile strength		ASTM D-638	140 Mpa
bending strength		ASTM D-790	200 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	7 kg·cm/cm(J/M)ft·lb/in
Bending modulus	23°C	ISO 178	22000 Mpa
Shore hardness		ASTM D-785	123 洛氏
Taber abraser	1000Cycles	ISO 9352	70.0 mg
Impact strength of cantilever beam gap	Unnotched23℃	ASTM D-256	20 KJ/m
bending strength		ASTM D-790	17.6 GPa
Bending modulus		ASTM D790/ISO 178	22 kg/cm²(MPa)[Lb/in²]
tensile strength	Yield,23°C	ISO 527-2	115 Mpa
Friction coefficient	对钢	ASTM D-1894	0.30
limiting pv value		东丽法	815 KJ/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
Linear coefficient of thermal expansion	垂重方向	ASTM D-696	2.4
Melting temperature		ISO 11357-3	278 °C
Combustibility		UL -94	V-0
Hot deformation temperature	1.82MPa	ASTM D-648	>260 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	260 °C
Melting temperature		DSC	278 °C
Melting temperature				278 ℃（℉）
Linear coefficient of thermal expansion	TD	ISO 11359-2	2E-05 cm/cm/°C
Combustibility (rate)		UL 94	V-0
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.9 mm/mm.℃
		MD	ISO 11359-2	1.9E-05 cm/cm/°C
		Flow	ASTM D-696	1.6

Physical properties	Phương pháp kiểm tra	TORAY JAPAN/A310M
Shrinkage rate	ASTM D955	0.5 %
density	ASTM D792/ISO 1183	2.06
Water absorption rate	ASTM D570/ISO 62	0.02 %

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
Shrinkage rate	TD:3.00mm2	Internal Method	0.50 %
		MD:3.00mm4	Internal Method	0.20 %
		Flow	东丽法	0.15 %
Water absorption rate	23°C,24hr	ISO 62	0.020 %
Shrinkage rate	垂重方向	东丽法	0.55 %
	320℃,98MPa,1mm厚，Flow长	东丽法	90

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
Dielectric strength		ASTM D-149	15 MV/m
Dielectric constant		ASTM D150/IEC 60250	5
Volume resistivity		IEC 60093	1E+16 ohms·cm
Dielectric strength		IEC 60243-1	22 KV/mm
Dielectric constant	10	ASTM D-150	5.8
Dielectric constant		23°C,1MHz	IEC 60250	5.00
Induced positive connection	10	ASTM D-150	0.002
Arc resistance	W电极	ASTM D-495	182 秒
Inherent resistance of volume		ASTM D-257	10 Ω.m
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Volume resistivity		ASTM D257/IEC 60093	1014 Ω.cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
Rockwell hardness	R-Scale	ISO 2039-2	123

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	TORAY JAPAN/A310M
BarFlowLength	320°C,1.00mm	Internal Method	9.00 CM