So sánh vật liệu
Thông số kỹ thuật
impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 12 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
-30°C | ISO 179/1eA | 14 kJ/m² |
flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
Burning rate | 1.00mm | ISO 3795 | 50 mm/min |
UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
FMVSS flammability | FMVSS302 | B | |
UL flame retardant rating | 0.8mm | UL 94 | HB |
1.5mm | UL 94 | HB | |
Atomization | refraction,F值 | ISO 6452 | 91 % |
mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Nominal tensile fracture strain | ISO 527-2 | 45 % | |
bending strength | 3.5%Strain | ISO 178 | 77.0 Mpa |
Poisson's ratio | ISO 527 | 0.35 | |
Tensile creep modulus | 1hr | ISO 899-1 | 2700 Mpa |
Tensile modulus | ISO 527-2 | 2950 Mpa | |
Tensile strain | Yield | ISO 527-2 | 25 % |
Bending modulus | ISO 178 | 2850 Mpa | |
tensile strength | Yield | ISO 527-2 | 71.0 Mpa |
Tensile creep modulus | 1000hr | ISO 899-1 | 1500 Mpa |
thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Linear coefficient of thermal expansion | TD:AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |
Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 155 °C |
Melting temperature | ISO 11357-3 | 178 °C | |
Linear coefficient of thermal expansion | TD:-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C |
Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 95.0 °C |
Linear coefficient of thermal expansion | MD:-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
Vicat softening temperature | -- | ISO 306/B50 | 160 °C |
Linear coefficient of thermal expansion | TD:AnnealingTemperature | ISO 11359-2 | 160 °C |
MD:-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
TD:-- | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
Vicat softening temperature | -- | ISO 306/A50 | 175 °C |
Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Shrinkage rate | MD | ISO 294-4 | 2.2 % |
ThermalConductivityofMelt | 0.22 W/m/K | ||
SpecificHeatCapacity of Melt | 3000 J/kg/°C | ||
density | ISO 1183 | 1.42 g/cm³ | |
Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.30 % |
melt mass-flow rate | ISO 1133 | 2.6 g/10min | |
MediumDensity | 1.19 g/cm³ | ||
Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 2.20 cm3/10min |
Shrinkage rate | TD | ISO 294-4 | 1.9 % |
Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 1.4 % |
Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Dissipation factor | 1MHz | IEC 60250 | 5.5E-03 |
Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
Dielectric strength | IEC 60243-1 | 41 KV/mm | |
Relative permittivity | 100Hz | IEC 60250 | 3.90 |
Dissipation factor | 100Hz | IEC 60250 | 3.5E-03 |
Compared to the anti leakage trace index | IEC 60112 | V | |
Surface resistivity | IEC 60093 | 2E+13 ohms | |
Relative permittivity | 1MHz | IEC 60250 | 3.90 |
hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
Rockwell hardness | M-Sale | ISO 2039-2 | 88 |
R-Sale | ISO 2039-2 | 119 |
Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | DUPONT NETHERLANDS/100PE BK602 |
---|---|---|---|
EmissionofOrganicCompounds | VDA277 | 4.70 µgC/g | |
Emission | VDA275 | <8.00 mg/kg |